黄娣-毕业论文预案.doc

摘 要 树脂砂的应用引发了铸造生产工艺的一次革命。随着社会的发展，低污染甚至无污染的造型材料必将成为行业的主流。CO2硬化碱性酚醛树脂粘结剂作为绿色的铸造粘结剂，其较高的强度性能使其成为拥有宽广市场潜力和价值的造型材料。 本课题采用的树脂合成工艺为碱性法分段升温滴定合成工艺 Abstract The application of resin sand triggered a revolution of the casting production process. With the development of society, non-polluting materials will become the mainstream of modeling industry. CO2-cured alkaline phenolic resin binder as a green binder foundry, its high strength properties make it have broad potential market and value of modeling materials. The resin process of this paper is sub-warming titration method synthesis. This process is basis resin for the synthesis of the resin matrix resin. This paper focuses on the type of cross-linking agent and the amount of system-depth study. In the experiment, the compression strength is the main factor in test. Inspected the joined amount of alkali, the silicon hydride, the borax, the sodiumstannate, the sodium aluminate to the coregranulated substance compressive strength influence，and obtained best joined quantity of allocated proportion, it has made the cementing agent which can be used in produce. Moreover, studied the amount of the A medicinal preparation , the experiment has indicated the A medicinal preparation can enormous enhance core granulatedsubstance intensity enormously. This article also analyse the research to the CO2 hardeningalkalinity phenolics air flush craft and its the solidificationmechanism. In the experiment , the best air flush time and the air flush current capacity has obtained. Meanwhile, carried on the shopcharacteristics test to the CO2 hardening alkalinity phenolicscementing agent, including the period of revolution, the sended spirit amount, and dispersed the nature and the joined quantity of the resin and so on, it has improven superiority of the CO2-hardening alkalinityphenolics cementing agent performance. In the economical analysis, compared this kind of CO2 hardeningalkalinity phenolics cementing agent with the general triet