放电等离子体烧结TiO2Al2O3复合陶瓷的高频介电性能.pdf

放电等离子体烧结Ti02．A1203复合陶瓷的高频介电性能 鲁燕萍 (北京真空电子技术研究所，北京100016) of Dielectric Ti02-A1203 Highfrequency properties composite ceramicsinteredSPS by Lu Yanping VacuumElectronicsResearch (Beijing Institute，Beijing100016，China) was Abstract：Inthis mixtureof and with additives paper,the T102 A1203powdersappropriate sintered andSPS thedielectric ofthe byfasbspeedfiringprocess techniques，respectively．Andproperties sinteredbodiesin weremeasuredtransmission／reflectionmethod．Itisconfirmedthat hi曲frequencies by tO SPS isbeneflcialuniformfine microstructure，thus technique get grains increasinghighfrequency lossof is tOits dielectric Ti02一A1203 ceramic，which composite advantageous behaviorin high frequency． Keywords：Fast-speedfiringprocess；SPStechniques；Dielectricproperties 摘要：本文分别用快速烧成工艺和放电等离子体烧结技术对添加适当添加剂的Ti02和舢203 粉体混合物进行烧结。利用反射，传输法测试了烧结体的高频介电性能。实验证实SPS烧结技术有 利于获得均匀的细晶结构，从而增加了Ti02-A1203复合陶瓷的高频介质损耗，介质损耗的增加有利 于Ti02一舢203复合陶瓷的高频吸波性能。 关键词：快速烧结；放电等离子体烧结技术；介电性能 微波吸收材料在微波管中有很重要应用。用于微波管的微波吸收材料通常称为衰减材料。微波 管内用体衰减材料大体上可分为导体．介质型、半导体一介质型和导体．半导体．介质复合型衰减材料， 其中导体或半导体是主要的衰减剂，它们分散在介质相中。导体可以是Mo、Fe、Co、Ni金属或其 混合粉末(添加、Ni等磁性粉体的吸波材料一般用于磁控管中或作为吸波涂料)，半导体可以是Ti02 或SiC相等；介质可以是A1203、MgO、A1N等无机介质材料或高分子有机材料。 图1典型Ti02一A1203复合衰减陶瓷微观结构图2Ti02一A1203复合衰减陶瓷微观结构