混凝土文献综述周爱鹏159912007.doc

高等混凝土结构课程 文献综述 钢纤维再生混凝土力学性能研究（抗压） 专业名称 结构工程 学生姓名 周爱鹏 学号 159912007 2016年3月1日 钢纤维再生混凝土力学性能研究（抗压） 摘要：据统计，每平方米拆除旧建筑物将产生7000-12000t建筑垃圾，将废弃的混凝土经过破碎，清洗和分级后，按照一定的配合比，制作以再生骨料为主的混凝土，简称再生混凝土。然而，再生混凝土与普通混凝土相比，抗压、抗拉强度较低，限制了其应用范围。在实验中向再生骨料混凝土添加钢纤维，以起到增强增韧的效果，改善其力学性能，对再生骨料混凝土的应用具有积极意义【3】。 关键词：钢纤维; 再生混凝土; 力学性能 Abstract: according to the statistics, of every square metre demolition of old buildings to generate $7000-12000 t construction waste, the waste concrete after crushing, washing and classification, according to a certain mixing ratio, production is given priority to with recycled aggregate concrete, recycled concrete for short. However, recycled concrete compared with ordinary concrete, compressive strength, tensile strength is low, limiting its application scope. In the experiment to the recycled aggregate concrete adding steel fiber, with the effect of enhanced toughening, improve its mechanical properties, the application of recycled aggregate concrete has positive significance. Keywords: steel fibre; Recycled concrete; Mechanical properties 一、引言 再生混凝土骨料是从已经拆除的建筑工程和桥梁中的建筑废渣，经过过筛、清洗得到的。破碎、拆解时，原有的混凝土结合体会被随机分解，在筛选时就会出现三类再生骨料：砂浆块、砂浆与卵石（砾石）的混合物、含有极少量砂浆的卵石（砾石）。工程应用表明，通过对再生骨料进行研磨和分类回收，可以改善其粒形、分离硬化水泥砂浆，从而提高其表观密度，降低吸水率。但是这种方法在多数一般的土木工程成本比较高，使用的范围比较小。针对这种情况，在工程上，最好的办法就是在再生混凝土中加入适量的钢纤维【1】，用钢纤维的抗拉强度来弥补再生再生混凝土自身强度不足的缺点。本文主要研究钢纤维对再生混凝土抗压性能的影响，考虑了1.钢纤维的掺比率2.再生粗骨料取代率3.再生混凝土强度的等级3个因素。 二、钢纤维掺比率的确定 与天然碎石相比，再生粗骨料密度低、孔隙率高，压碎指标大，骨料本身强度较低：骨料和新、旧砂浆面存在裂缝外，新、旧砂浆本身存在较多的裂缝，且都相互贯穿起来，形成强度低的薄弱区。另外，掺加钢纤维对混凝土的抗压强度有一定提高，这主要与钢纤维的特性有关，钢纤维均匀地分散于基体混凝土中，并通过分散的钢纤维，减小因荷载在基体混凝土引起的细裂缝端部的应力集中，从而控制混凝土裂缝的扩展，并在混凝土的受力破坏过程中吸收大量能量的作用，提高纤维再生混凝土的抗压强度，弥补再生骨料的内部缺陷。实验对比结果表明如下【1】： 1.钢纤维再生混凝土立方体抗压强度略低于相应的钢纤维天然混凝土。 2.再生混凝土中加入钢纤维后抗压强度得到较明显提高（10%左右），且随着钢纤维从0.5%提到1.5%。其抗压强度呈非显现提高。当钢纤维为（1%～1.5%）提高幅度较大。但国内外研究表明，并非所加入钢纤维率越大混凝土构件的抗压能力提高越多。超过2%时特别到3%时，就不太明显效果。而且粘合协同工作会受影响【2】。 3.当钢纤维掺率为1%时，钢纤维会发挥最好的力学效果，并且此时对外界能量的吸收达到最大值。钢纤维与再生混凝土可较好粘结，共同作用时能有效的阻滞、减缓裂缝的发