ホウ酸処理木材の表面燃焼性および耐火性.pdfVIP

－研究－ ホウ酸処理木材の表面燃焼性および耐火性 菊地 伸一 駒澤 克己 峯木 安信＊1 Surface Flammability and Fire Endurance of Wooden Materials Treated with Boric Acid Shin'ichi KIKUCHI Katsumi KOMAZAWA Yasunobu MINEKI The ignitability，the surface flammability and the fire endurance have been measured fo rwood treatedwithahighconcentratedsolutionofboricacid．Boricacidandsodiumoctaboratepreventedthe ignition of plywood．However，they were less efftctive than treatment with ammonium phosphate or ammonium bromide．The plywood treated with boric acid did not meet the standards of internal finish material with respect to TC and after flame time．When 15 parts of ammonium bromide was added， noncombustibility was improved and the treated plywood met the standards．The thermal insulation property was improved with the boric acid treatment and it was found to increase about 20％． Keywords ： ignitability，fire-retardant treatment，thermal insulation property， sodium octaborate 着火性，難燃処理，遮熱性，八ホウ酸ナトリウム ホウ酸の高濃度溶液で処理した木材の着火性，表面燃焼性および耐火性を検討した。ホウ酸およ び八ホウ酸ナトリウムは着火を抑制したが，リン酸アンモニウム，臭化アンモニウムの効果を下回 るものであった。ホウ酸高濃度溶液による処理だけでは，建築防火内装材料の規格値を満足しな かった。しかし，臭化アンモニウムを添加すると性能は大幅に向上した。 さらに，ホウ酸処理によって木材の遮熱性能は約20％程度向上した。 1． はじめに 木材やセルロース系材料を難燃化するには，リン 建築基準法では燃えやすい材料や有害ガスを発生 酸アンモニウムを始めとするリン化合物および臭化 させる材料を建築物の内装に使用することを制限し アンモニウムを始めとするハロゲン化合物が顕著な ている。したがって，木材を大規模なホールや集会 効果を示す。 場の内装に利用する場合，一定の防火基準を満たす ホウ素系化合物の難燃効果もよく知られ，ホウ砂? 難燃処理が必要となる。このため，数多くの木材用 ホウ酸混合物は発炎燃焼と赤熱燃焼を抑制できると 難燃剤および処理方法が提案されてきた。また，近 されている。薬剤の安全性が高いことから，セルロー 5-8) 年では地場産材の有効活用の一策として難燃加工が