第36卷第5期 湖南大学学报(自然科学版) v01．36，N0．5 2 0 0 9年5月 Journal of Hunan University(Natural Sciences) May．2 0 0 9 文章编号：1674．2974{2009)05．0016．05 EMC技术对RPC流动度及强度的影响+ 胡检，黄政字’，马 宁 (湖南大学土木工程学院，湖南长沙410082) 摘要：EMC(Energetically Modified Cement)技术是一项基于粉磨工艺的新技术．其对 RPC性能的影响目前尚不明确．试验研究了EMC技术的使用对RPC流动度和各类型高效 减水剂的最佳掺量的影响，同时通过试验探讨了EMC技术对RPC各龄期和不同水胶比下 强度的影响．试验结果表明，EMC技术的使用使硪)c的流动度降低，且使高效减水荆的最 佳掺量也稍有降低，使用萘系减水剂更为明显；另一方面，使用EMC技术后，RPC的l d的 抗压和抗折强度分别提高了103．4％和27．2％，28 d则分别提高了25．1％和36．6％；同时 EMC技术降低了强度对各种因素如水胶比大小等的敏感性． 关键词：EMC技术；活性混凝土；流动度；强度 中图分类号：TU528 文献标识码：A Effects of EMC Technology on the Fluidity and Strength of RPC HU Jian，HUANG Zheng-Ⅳ，MA Ning (College of Civil Engineering，Hunan Univ．CharI秘ha，Hunan 410082，China) Abstract：The Energetically Modified Cement(EMC)is a new technology based on grinding。However，the effects of EMC technology on the performance are unclear．Based on experiments，the effects on the fluidity of RPC by the EMC technology were discussed．8,8 well as the optimal quantity of the water-reducing admixtures used in experiments．Meanwhile，experiments were performed to study the impact on the strength of褂)C by the EM[C technology，including every age strength and those of Reactive Powder Concrete(RPC)made by dif— ferent water to binder ratio．The results showed that the EMC technology lowered the RPC fluidity and the op． ritual quantity of the water．reducing admixtures，which is particalarly obvious for FDN．The oompressive strength of RPC in 1 day WaS increased by 103．4％because of the rise of EMC technology．while the value of flexu础strength was 27．2％．The corresponding ones in 28 days were 25．1％and 36．6％respectively．Be— sides，EMC technology reduced the degree of relationship between strength and the water to binder ratio． Key words：EMC technology；RPC：fluidity；strength RPC(活性粉末混凝土)是20世纪末由法国研 究成功的一种超高强低脆性，耐久性优异并具有广 阔前景的新型混凝土，它是由级配细砂(不含粗骨 料)、水泥、石英粉、硅灰和超塑化剂(或加钢纤维)组 成，在凝结硬化过程中采取适当的成型养护工艺如 加压、加热而获得?．EMC(Energetically Modified Cement)技术是一项基于粉磨工艺的新技术[2]2，将 水泥与各种不同的掺合料或外加剂混合，通过特殊 处理使其能量结构发生改变从