多道焊三维残余应力场有限元模拟.pdfVIP

p研究简报p 多道焊三维残余应力场有限元模拟 * SIMULATION OF 3D RESIDUAL STRESSES FIELD OF MULTI-PASS WELDING BY FEM 倪红芳** 凌 祥 涂善东 (南京工业大学 机械与动力工程学院,南京 210009) NI HongFang LING Xiang TU ShanTong ( College of Mechanical and Power Engineering , Nanjing University of Technology , Nanjing 210009, China) 摘要 运用大型有限元计算软件 ABAQUS, 对 316L不锈钢平板多道焊接头的温度场和残余应力场进行模拟。有限 元模型中选用三维实体单元,考虑材料物理性能随温度的变化和周边对流、辐射散热的影响。运用内生热的加载方法模 拟焊接热源,运用单元激活技术模拟多道焊焊接过程。获得了三维多道焊焊接温度场和残余应力场,并对计算结果进行 分析。 关键词 多道焊 有限元模拟 温度场 残余应力场 中图分类号 TG404 TB115 Abstract Temperature and stress field of 316L stainless steel is simulated by FEM using ABAQUS codes. The 3-D solid elements are used in FEM model, and temperature depended material properties are considered as well as the convection and radiation as boundary conditions1 Internal heat generation loading method is applied to simulate heat source, and model change ability to simulate mult-i pass weld1 The temperature field and residual stress field of 3-D mult-i pass weld are obtained, and the results are discusses1 Key words Multi-pass welding; Simulation by finite element method; Temperature field; Residual stress field Corresponding author : LING Xiang, E-mail: xling@njut. edu. cn, Fax : + 86-25-3600956 The project supported by the Natural Science Foundation of Jiangsu Province of China ( No1 BK2001098)1 Manuscript received in revised form 1 引言 大量失效研究表明, 焊接残余应力是压力容器发 生应力腐蚀开裂 [ 1~ 7] 的主要原因之一,因此, 为保证设 备安全运行,必须设法消除焊接残余应力。而获得焊 接残余应力分布规律,对消除焊接残余应力十分重要。 由于焊接残余应力的复杂性,目前主要采取数值模拟 的方法来获得残余应力的分布规律, 也有许多研究者 采用实验测量的方法。应用有限元方法模拟焊接温度 场和残余应力场, 国内外许多学者已做了大量工作。 鉴于焊接过程的复杂性, 这些分析大多采用简化模型, 如轴对称单元或二维平面假设 [ 8~ 11] , 从而使计算结果 与真实情况相差很大。在进行三维模拟时, 目前国内 所作工作重点在单道焊的分析 [ 12~ 14] 。对于三维多道 焊的模拟相关文献较少, 国外曾经有学者用壳体单元 或轴对称 [ 15] 模型做过分析。 以下尝试应用大型有限元计算软件 ABAQUS, 采 用三维实体单元和运用单元激活技术对 316L 不锈钢 平板多道焊焊接接头的温度场和残余应力场进行模 拟,以期获得焊接接头的三维温度场和残余应力场,为 进一步研究消除焊接残余应力的方法提供参考。 2 焊接物理模型的建立[ 13] 211 温度场控制方程 在区域 8 中热过程控制方程为 cp dT dt = [? K? T ] + ?Q ( 1) 式中 c p为比热, K为导热系数, ?Q 为内热源强度, T 为 温度, t为时间。 焊接温度场控制方程的热流