Comparison of the strength and durability performance.pdf

下载文档

7
0
约4万字
约 10页
2017-04-11 发布于江苏
举报
版权申诉
保障服务

Comparison of the strength and durability performance.pdf

1、本文档共10页，可阅读全部内容。
2、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。
3、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击这里二次下载。
4、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。

Comparison of the strength and durability performance

Comparison of the strength and durability performance of normal- and high-strength pozzolanic concretes at elevated temperatures Chi-Sun Poon*, Salman Azhar, Mike Anson, Yuk-Lung Wong Department of Civil and Structural Engineering, Research Center for Advanced Technology in Structural Engineering, The Hong Kong Polytechnic University, Hung Hom, Hong Kong, China Received 7 August 2000; accepted 18 June 2001 Abstract The strength and durability performance of normal- and high-strength pozzolanic concretes incorporating silica fume, fly ash, and blast furnace slag was compared at elevated temperatures up to 800C. The strength properties were determined using an unstressed residual compressive strength test, while durability was investigated by rapid chloride diffusion test, mercury intrusion porosimetry (MIP), and crack pattern observations. It was found that pozzolanic concretes containing fly ash and blast furnace slag give the best performance particularly at temperatures below 600C as compared to the pure cement concretes. Explosive spalling occurred in most high-strength concretes (HSCs) containing silica fume. A distributed network of fine cracks was observed in all fly ash and blast furnace slag concretes, but no spalling or splitting occurred. The high-strength pozzolanic concretes showed a severe loss in permeability-related durability than the compressive strength loss. Thirty percent replacement of cement by fly ash in HSC and 40% replacement of cement by blast furnace slag in normal- strength concrete (NSC) was found to be optimal to retain maximum strength and durability after high temperatures. D 2001 Elsevier Science Ltd. All rights reserved. Keywords: High temperature; Pozzolan; Compressive strength; Permeability; Microstructure 1. Introduction Pozzolanic concretes are used extensively throughout the world; the oil, gas, nuclear, and power industries are among the major users. The applications of such concretes are increasing day by day due to their s