带铝硅镀层硼钢板的热冲压成形性探究.pdfVIP

壹 Availbe onlie atw．sciendirect．om ·：j，ScnDPress Trans．Nonferous Met．Soc．China 24(2014)1750—1757 Transaetions of Nonferrous Metals Society of China w w w ．tnm sc．ca Formability of aluminum-silicon coated boron steel in hot stamping process Zhong—xiang GUI ’。，Wei-kang LIANG ’ ，Yi—sheng ZHANG ’ 1．State Key Laboratory of Material Processing and Die and Mould Technology, Huazhong University of Science and Technology,Wuhan 430074，China； 2．College of Materials Science and Engineering，Huazhong University of Science and Technology, Wuhan 430074，China Received 27 June 2013；accepted 3 October 2013 Abstract：Flow behavior of the A1-Si coated boron stee1 was investigated with Gleeble一3500．in comparison with the uncoated one． Efrect Of deformation conditions on the coating integrity was characterized by optical microscopy．Facture surfaces of the coated steels were inspected under SEM．Experimenta1 results indicate that the ultimate tensile strength and ductility of the A1-Si coated boron steel are lower than those Of the un coated steel un der test conditions．Extensive cracks occur in the coating after tensile tests； the width and density of cracks are sensitive to the deformation temperatures and strain rates．The bare substrate exposed between the separate coating segments is oxidized．Appearance of the oxide degrades the A1-Si coating adhesion．Remarkable diference betw een formability of the coating layer and the substrate is confirmed．The form ability of the A1-Si coating could be optimized by controlling the phase tran sformation of the ductile FeIrich interm etallic compounds wifhin it during the austenization． Kev words：hot stamping；boron steel；oxidation；A1-Si coating；crack；formability 1 Introduction Hot stamping of the boron steel has proved a success for automotive manufacturers， owing to its abilit、，to achieve the purpose of reduction of both the vehicle weight and fuel consumption，while ireproves the safety and crashworthiness qualities at the same time [1，2]．And t