疲勞分析.pptVIP

Stress-Life (S-N) Theory;Stress-Life (S-N) Theory;Some Definitions;输入应力循环 Input is cycles of STRESS 即高周疲劳或名义应力疲劳法 Also known as “High Cycle Fatigue” or “Nominal Stress Approach” 尽管在临界区域的局部应力会是塑性的但名义应力循环必须为弹性应力(因此为高周疲劳） Nominal stress cycles must be elastic (hence high cycle) though local stresses at the critical location will be plastic 在MSC/FATIGUE SN分析中有限元弹性计算结果可直接利用（无塑性修正） In MSC/FATIGUE SN analysis, elastic FE results are used directly (no plasticity correction);S-N Curve;沃勒疲劳实验机 Wohler’s Railway Component Test Rig (1852 to 1870);S;S-N Approach;S-N Approach;S-N Curves;S-N Curves;Material S-N Curves;S-N曲线的离散性 Scatter in S-N curves;部件S-N曲线 Component S-N curves;部件S-N曲线可以使用远端的名义应力进行疲劳分析Component S-N Curves may use remote or nominal stress;Static Limitations;S-N Method - Similitude;S-N方法假定零件或部件的寿命在同一名义应力下与测试试样一致 The S-N method assumes that the life of a component or structure is the same as that of a laboratory test specimen if both are subject to the same nominal stresses. 如果在结构中存在与实验条件不一致，需要进行修正（如平均应力、环境、表面处理等因素） If the conditions in the test are different to those in the structure, similitude breaks down, and we need to make corrections for factors such as mean stress, environment, surface finish, etc.;对变幅载荷的处理-迈因纳线性累积损伤法则和雨流记数 Handling Variable Amplitude Loads - Miner’s Rule and Rainflow Counting; 名义应力有限寿命设计法是一种较早使用的有限寿命设计法，它是无限寿命设计法的直接发展，两者的基本设计参数都是名义应力。其设计思想也大体相似，都是从材料的S-N曲线出发，再考虑各种影响因素，得到零件的S-N曲线，并根据零件的S-N曲线进行疲劳设计。 所不同的是，无限寿命设计法使用的是S-N曲线的右段-水平部分，亦即疲劳极限；而有限寿命设计法使用的是S-N曲线的左段-斜线部分，亦即有限寿命部分。而有限寿命设计的设计应力一般都高于疲劳极限，这时就不能只考虑最高应力，而需要按照一定的累积损伤理论估算总的疲劳损伤。; 累积损伤是有限寿命设计的核心问题。最早进行疲劳累积损伤研究的学者是Palmgren（帕尔姆格伦），他于1924年在估算滚动轴承寿命时，假设损伤累积与转动次数成线性关系，首先提出了疲劳损伤积累是线性的假设。其后，M.A. Miner（迈因纳）于1945年又将此理论公式化，形成了著名的Palmgren- Miner线性累积损伤法则。 但以后的研究发现，由于Miner法则没有考虑到加载顺序对疲劳寿命的影响，因此它估算出的疲劳寿命与实际寿命有较大的出入。于是许多学者又提出了一些新的累积损伤理论，其中比较著名的有Corten-Dolan理论与双线性理论。;Miner’s Rule - Block Loading;Variable Amplitude Loads - Estimating Lifetime -; Stress or Strain Cycles:;计数法;Rainflow Cycle Coun