施工技术刊载水泥基灌浆料产品的发展1.docVIP

PAGE  PAGE 6 水泥基灌浆料的发展 朱卫华 （上海宝冶工程技术有限公司 上海 200941） 【摘要】：水泥基灌浆料加水拌合后具有流动性好、微膨胀、早期和后期强度高、不泌水等性能。论述了灌浆料相关标准的发展过程，以及材料性能的发展情况。经过多年的快速发展，高强无收缩灌浆料除了在设备基础二次灌浆上应用外，已经在混凝土结构改造和加固工程及铁路桥梁工程中广泛应用。 【关键词】：建筑材料；灌浆料；标准；应用 【中图分类号】TU521.26 【文献标识码】A 【文章编号】1002-8498（2009）06-0076-02 Development of Cement-based Grouting Material Zhu Weihua (Shanghai Baoye Engineering Technology Co.,Ltd. ,Shanghai 200941,China) Abstract: Cement-based grouting material mixed with water has some characteristics of good fluidity, micro-expansibility, high early and later strength and no bleeding. The author shows developing procedure of correlation standards on grouting material, and developing condition of performances of grouting material. With quickly developing for many years, high-strength no-shrinkage grouting material has used widely in rebuilding and strengthening engineering of concrete structure and railway and bridge engineering, besides secondly grouting of equipment basement. Key words: building material; grouting material; standard;application 水泥基灌浆料与传统的细石混凝土相比，具有流动性更好、强度更高和施工易于控制的特点；与传统的环氧砂浆相比，具有膨胀性好，施工简便快捷等特点。自20世纪90年代初，我国自主研发生产的水泥基灌浆材料在众多大中型企业的设备安装、建筑结构加固改造工程中得到广泛应用。 目前国内从事水泥基灌浆材料的生产企业达200余家，年产量近50万t。近年来,由于新材料发展日新月异，新的外加剂如雨后春笋，我国灌浆料的技术性能飞速提高，其各项技术性能已达到国际水平。而灌浆料的使用范围，已逐渐从早期单一的冶金建设全面拓展到市政、环保、港口、电力、造纸等各行业，并获得了良好的效果。 1 水泥基灌浆料技术发展 水泥基灌浆材料是一种由水泥、集料（或不含集料）、外加剂和矿物掺合料等原材料，经工厂化配制生产而成的具有合理级配的干混料。加水拌合均匀后具有可灌注的流动性、微膨胀、高的早期和后期强度、不泌水等性能。 1.1相关标准的发展 1）1998年3月28日，原冶金工业部发布了针对水泥基灌浆材料的第一部标准行业标准《水泥基灌浆材料施工技术规程》（YB/T9261-98），首次系统地明确了灌浆工艺及要求； 2）2005年4月11日，国家发展和改革委员会发布了建材行业标准《水泥基灌浆材料》（JC/T986-2005）。 3）2008年3月31日，中国住房和城乡建设部与国家质量监督检验检疫总局联合发布了国家标准《水泥基灌浆材料应用技术规范》（GB/T50448-2008），系统地对灌浆工程的设计、施工、质量控制与工程验收提出了具体要求。 1.2 灌浆料性能指标的发展 灌浆料产品性能近年来发展很快，尤其是流动度等各项指标。以上海宝冶工程技术有限公司生产的BY系列灌浆料为例，在20世纪90年代其流动度指标指标一直沿袭日本“塔斯库”的方法，用“s”来计量。后来随着国内相关规范及标准的出台，统一使用“mm”作为流动度的计量单位，用行星式水泥胶砂搅拌机和截锥圆模（下口内径（100±0.5）mm,上口内径（70±0.5）mm，高（60±0.5）mm）等仪器。BY系列灌浆料的主要性能指标如表1所示。 随着冬期施工工艺的发展，对用于冬期施工的灌浆料性能指标也提出了明确要求，如表2