SnSb15合金液-液结构转变的可逆性及熔体状态对凝固的影响.pdfVIP

第 23 卷第 6 期 中国有色金属学报  2013 年 6 月  Vol.23 No.6  The Chinese Journal of Nonferrous Metals  June 2013  文章编号：1004­0609(2013)06­1586­05  SnSb15 合金液−液结构转变的 可逆性及熔体状态对凝固的影响 高文龙，张先锋，丰大顺，祖方遒  (合肥工业大学 材料科学与工程学院，合肥  230009)  摘 要：为了探讨液−液结构转变的可逆性及熔体状态对凝固的影响，利用直流四电极法测量 SnSb15合金熔体在 三轮连续升降温过程中的电阻率−温度曲线。分析 SnSb15合金熔体的不可逆和可逆转变的物理内涵，进而讨论不 可逆转变对凝固影响的作用机制。结果表明：SnSb15合金熔体发生了温度诱导的液−液结构转变，其首轮升温过 程的转变呈不可逆性，而后续降温及升温过程的转变呈可逆特征；且首轮升温过程的不可逆液−液结构转变显著 影响合金的凝固行为和组织， 如初生相和包晶相的形核过冷度分别增大 9.7和 5℃， 凝固时间分别缩短 2.5和 4 s， 并且凝固组织明显细化。 关键词：SnSb15合金；液−液结构转变；可逆性；熔体状态；凝固行为；凝固组织 中图分类号：TG146.1  文献标志码：A  Reversibility of liquid­liquid structure transition and effects of  melt state on solidification of SnSb15 alloy  GAO Wen­long, ZHANG Xian­feng, FENG Da­shun, ZU Fang­qiu  (College of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China)  Abstract: In order to study the reversibility of liquid­liquid structure transition (L­LST) and the effects of melt state on  solidification,  the electrical resistivity­temperature  curves of SnSb15 melt were measured in  three heating and cooling  cycles by means of DC four­probe method. The physical connotation of irreversible and reversible L­LST was analyzed,  and the effects of irreversible L­LST on solidification were also discussed. The results show temperature induced L­LST  occurs in SnSb15 melt. L­LST in first heating process is irreversible, but it is reversible in subsequent cooling and heating  processes.  Besides,  irreversible  L­LST  can  significantly  affect  the  solidification  behavior  and  microstructure,  i.e.  the  undercooling degrees for primary and peritectic phase enlarge 9.7 and 5 ℃, the solidification time shortens 2.5 and 4 s,  respectively. Moreover, the solidification microstructures are refined obviously.  Key  words:  SnSb15  alloy;  liquid­liquid  structure  transition;  reversibility;  melt  state;  solidification  behavior;  solidification microstructure  Sn­Sb 二元合金是一种典型的包晶合金，其作为 轴承合金已被广泛地应用于机械工业，在电