aluminiumalsi10mg-Materialdatasheet.PDF
Material data sheet
EOS Aluminium AlSi10Mg
EOS Aluminium AlSi10Mg is an aluminium alloy in fine powder form which has been specially
optimised for processing on EOSINT M systems
This document provides information and data for parts built using EOS Aluminium AlSi10Mg
powder (EOS art.-no. 9011-0024) on the following system specifications:
- EOSINT M 280
with PSW 3.6 and Original EOS Parameterset AlSi10Mg_Speed 1.0
- EOS M 290 400Watt
with EOSPRINT 1.0 and Original EOS Parameterset AlSi10Mg_Speed 1.0
Description
AlSi10Mg is a typical casting alloy with good casting properties and is typically used for cast
parts with thin walls and complex geometry. It offers good strength, hardness and dynamic
properties and is therefore also used for parts subject to high loads. Parts in EOS Aluminium
AlSi10Mg are ideal for applications which require a combination of good thermal properties and
low weight. They can be machined, spark-eroded, welded, micro shot-peened, polished and
coated if required.
Conventionally cast components in this type of aluminium alloy are often heat treated to im-
prove the mechanical properties, for example using the T6 cycle of solution annealing,
quenching and age hardening. The laser-sintering process is characterized by extremely rapid
melting and re-solidification . This produces a metallurgy and corresponding mechanical proper-
ties in the as-built condition which is similar to T6 heat-treated cast parts. Therefore such
hardening heat treatments are not recommended for laser-sintered parts, but rather a stress re-
lieving cycle of 2 hours at 300 °C (572 °F). Due to the layerwise building method, the parts have
a certain anisotropy, which can be reduced or removed by appropriate heat treatment - see
Technical Data for examples.
EOS GmbH - Electro Optical Systems
Robert-Stirling-Ring 1
您可能关注的文档
- 3材料的析晶温度测定.PDF
- 4-氨基联苯与人体血红蛋白体外加合反应及加合物测定的研究.PDF
- 40.空虚的原子.PDF
- 4050流动人口协管员考试复习资料.doc
- 49电子和场综合实验(电子束实验).PDF
- 4GLTE流动通讯客户).PDF
- 5g945756.PDF
- 607家淀粉厂乱排污被拿下.PDF
- 614专业基础综合A考试时间.PDF
- 6xschuko,aluminium.PDF
- 分析let s单元56ago2卷纸zheng unit56.pdf
- 塑胶材料其它分类原料pa9t 12.pdf
- md16x16数字媒体切换器设备.pdf
- 者参考项目发起人学科类型单位序列承包商修订页代码顺序典型.pdf
- 届世界天然气大会阿姆斯特丹2006add10288.pdf
- 期测试记录表每周weekly g1g6 journeys tests level 6 lesson26.pdf
- modernize-whitepaper现代化您应用程序白皮书.pdf
- anybackup产品典型案例分析.pdf
- 约克金融工程课程tfeslide32.pdf
- 广州市妇女儿童医疗中心历份教学药历01tjy.pdf
文档评论(0)