温拌沥青混合料设计方法与路用性能研究.docVIP

Hans Journal of Civil Engineering 土木工程, 2013, 2, 1-9 /10.12677/hjce.2013.21001 Published Online February 2013 (/journal/hjce.html) Research on the Performance and Design Method of Warm Asphalt Mixture Fei Huang , Hao Ju 1 2 1 Nanjing Highway Construction Department, Nanjing 2 Urban Roads Research Center of Nanjing, Nanjing Email: vivian_jh@163.com Received: Nov. 23 , 2012; revised: Dec. 26 , 2012; accepted: Jan. 8 , 2013 rd th th Abstract: In this paper, research is carried out on the compaction characteristics, design methods and performance of the surfactant class warm mix technology. Warm mix asphalt molding methods and performance evaluation are focused. AC, SMA, UTA and SUP are chosen with ordinary asphalt and modified asphalt to evaluate performance of warm mix- ture respectively. Keywords: Surfactant; Warm Asphalt; Design Method; Pavement Performance 温拌沥青混合料设计方法与路用性能研究 1 菲，居浩 2 黄 1 南京市公路建设处，南京 南京市城市道路建设项目储备中心，南京 2 Email: vivian_jh@163.com 收稿日期：2012年 11月 23日；修回日期：2012年 12月 26日；录用日期：2013年 1月 8日 摘 要：针对表面活性类温拌技术的压实特性、设计方法以及性能开展了研究，重点确定了温拌沥青混合料的 成型方法和性能评价等方面内容。选择 AC、SMA、UTA和 SUP四类级配和普通沥青、改性沥青两种胶结料进 行温拌沥青混合料性能对比分析。 关键词：表面活性；温拌沥青；设计方法；路用性能 1.引言 材集团有限公司和同济大学等单位合作开始开展研 究温拌沥青混合料。起初研究的是乳化沥青温拌沥青 混合料，同年 10 月，在北京国道 110 支线成功实施 了我国第一条温拌沥青混合料试验路。一次为开端， 温拌技术在我国的研究应用逐步推广，以基于表面活 性剂的温拌沥青混合料占绝大部分。与国外的研究和 发展一样，我国基于表面活性剂的温拌沥青混合料也 经历了两个发展阶段，即乳化沥青温拌法和浓缩液温 拌法，浓缩液温拌出现后，乳化沥青温拌法就不在使 用了。 表面活性类 Evotherm 温拌技术是用一种特殊的 表面活性浓缩液，可以在常温下保存。该方法施工工 艺与热拌沥青混合料基本一致。用于生产这种温拌沥 青混合料的温拌剂，这些添加剂能够提高沥青与集料 的裹附能力，提高混合料的施工和易性以及粘聚能 力。浓缩液的水分在与高温集料拌和过程中就以水蒸 气的形态释放出去。拌和完毕的温拌沥青混合料从外 观上看其裹附和颜色与热拌沥青混合料没有什么差 [1] 别 。 2005年交通部公路科学研究院、北京市政路桥建 表面活性类 Evotherm温拌技术是用一种特殊的 Copyright ? 2013 Hanspub 1  温拌沥青混合料设计方法与路用性能研究 乳化沥青来实现温拌，可以在 80℃左右保存，该种乳 入预热至设计拌和温度的拌和锅内，用拌铲将集料拉 成一斜面，露出拌和锅底部，加入定量的改性沥青到 此位置，将称量好的 DAT浓缩液倒入沥青液面上， 见图 1；4)拌和 1.5 min，加入矿粉，再拌和 1.5