1024 高磷铁水的复吹转炉高效脱磷与高拉碳工艺研究与实践.pdf

2016 年（第十九届）全国炼钢学术会议论文集 高磷铁水的复吹转炉高效脱磷与高拉碳工艺研究与 实践 王杰，曾加庆，杨利彬，林腾昌，汪成义 （钢铁研究总院工艺研究所，北京，10081） 摘要：从理论和技术的角度分析了转炉高拉碳操作与铁水磷的高效脱除。提出“双渣法”在转炉冶炼前期高效脱磷，脱磷渣排 出，冶炼后期少渣高拉碳操作的操作工艺。在渣料消耗与渣量降低20% 的前提下，120t复吹转炉的工艺试验实现脱磷率94.72%， 终点出钢碳0.232% 。 关键字：脱磷，高拉碳，转炉； Research and Practice of BOF Efficient Dephosphorization and Catch Carbon Process of High Phosphorus Hot Metal WANG Jie, ZENG Jia-qing, YANG Li-bin ，LIN Teng-chang, WANG Cheng-yi （Central Iron and Steel Research Institute,Metallurgical Technology Institute,Beijing,10081 ） Abstract: Analysis on efficient dephosphorization and catch carbon process was made, from the point of theory and technology. View of which makes the efficient dephosphorization and catch carbon process in a single converter available was proposed, followed as efficient dephosphorization during the dephosphorization stage, pour-out of dephosphorization slag, less slag and catch carbon process of decarbonization stage. Trail experiments were made on 120t converter, dephosphorization rate of 94.72% and end point carbon of 0.232% were got, under the background of the slag amount and slag material assumption reduced by 20%. Key words: dephosphorization, catch carbon, converter. 转炉冶炼的主要任务为脱磷与脱碳升温。其中，脱磷是在转炉炼钢过程中必须解决的主要问题之一， [1] 可以说转炉新工艺技术开发多围绕转炉高效脱磷这个核心问题而展开 ；针对钢种含碳量不同，转炉终点控 [2] 制有增碳法 （低碳出钢）和高拉补吹 （高碳出钢）两种方法 。高碳出钢和低碳出钢相比具有耗氧量少、金 属收得率高、渣中FeO含量低、对炉衬的侵蚀小、钢中氧含量低、合金消耗少、原始夹杂物较少、钢中氮氢 [3] 等气体含量低等优势 。鉴于高碳出钢的一系列优点， 尤其是在提高钢水纯净度，提高产品质量上的好处， 某厂在120 t 转炉上开展了针对GCr15钢冶炼的高拉碳法冶炼工艺的生产研究。 1 转炉脱碳理论分析 [%O] mP /[%C] （1）