37水平连铸高压锅炉管用12Cr2MoWVTiB圆管坯工艺参数研究.5-6.doc

水平连铸高压锅炉管用12Cr2MoWVTiB圆管坯工艺参数研究 田汉蒲 徐景峰 （ 湖南衡阳钢管（集团）有限公司，湖南 衡阳 421001 ） 摘 要：研究了水平连铸生产∮130mm规格高压锅炉管用12Cr2MoWVTiB铸坯的主要工艺参数，分析了起铸失败、拉坯阻力大的原因，提出了钢中V、Ti、B等元素含量，起铸工艺，钢水过热度，结晶器锥度，反推量等是该钢种生产成功的关键因素，并给出了其适当的控制范围。 关键词：水平连铸；12Cr2MoWVTiB；圆管坯；参数研究 The study on technology parameter of Horizontal Continuous Cast 12Cr2MoWVTiB steel round billet for tube of high pressure boiler TIAN Han-pu , XU Jing-feng (Hunan Hengyang Steel Tube Co Ltd, Hengyang 421001) Abstract：The main technological parameter of 12Cr2MoWVTiB steel ∮130mm round billet for high pressure boiler tube has been studied, and analyzed the reason of beginning casting failure and large resistance to stripping, and proposed the key factor of succeed product was V、Ti、B content in steel, beginning casting process, liquid steel superheat, taper of mold, reverse-pushing, and advised the proper control area. Key words:Horizontal Continuous Cast; 12Cr2MoWVTiB;round billet;parameter study 1 前言 12Cr2MoWVTiB钢具有较高的使用温度（≤620℃）、良好的焊接性能及在高温下表现出的优良的力学性能、耐磨性及抗高温蠕变性等，被用在国产20万、30万千瓦火力发电机组的过热器和再热器上。国内年需求量约在6500吨左右，随着国家新一轮能源基础设施建设的展开，该钢种的市场前景将更为广阔。 衡阳钢管（集团）有限公司利用水平连续铸钢技术，对此钢种进行了研究开发。 12Cr2MoWVTiB钢化学成份及钢水准备 2.1 化学成份 YB/T 5137-1998《高压用无缝钢管圆管坯》规定12Cr2MoWVTiB钢的化学成份见表1。为最大程度满足钢的性能要求[1]，生产时制定了内控标准。包括对P、S及残余元素的含量均作出了规定。 表1 12Cr2MoWVTiB钢化学成份的标准及内控要求 Table 1 The criterion of chemical composition for 12Cr2MoWVTiB steel 元 素/% C Si Mn P S Cu Cr Mo 标准要求 0.08~0.15 0.45~0.75 0.45~0.65 ≤0.030 ≤0.030 ≤0.20 1.60~2.10 0.50~0.65 内控要求 0.08~0.12 0.50~0.65 0.50~0.65 ≤0.020 ≤0.010 ≤0.15 1.70~2.00 0.52~0.60 元 素/% Ti V B W Ni As+Sn+Sb+Pb+Bi 标准要求 0.08~0.18 0.28~0.42 0.002~0.008 0.30~0.55 内控要求 0.11~0.16 0.30~0.40 0.002~0.008 0.35~0.50 ≤0.25 ≤0.040 2.2 工艺路线 12Cr2MoWVTiB钢工艺路线为：EBT +LF+喂丝+VD+保护浇注+HCC。 3 水平连铸机的主要性能参数 连铸机型号 SLD-140 中间包容量 15t 机数×流数×台数 3机×2流×2台 流间距 　　　　 1200mm 冶金长度 10.5m 拉坯速度 ≤3.5m/min 铸坯规格 ∮110~∮180mm 切割方式