常压消失模铸造工艺在大扭曲叶轮生产中的应用.pdfVIP

学兔兔 Dec．2011 - 铸 造 Vo1．60 NO．12 FOUNDRY ·1203· {消失模铸造 { 、^● ’，■^，■■^ ’^■v■，■^，■ ■ ’^， 常压消失模铸造工艺在大扭曲叶轮生产中的应用 何立明 (大连深蓝泵业有限公司，辽宁大连116031) 摘要：分析了大扭曲叶轮的结构特点和技术要求，论述了常压消失模铸造叶轮工艺，探讨了叶轮消失模铸造过程中应 注意的问题。经生产验证，用常压消失模铸造生产大扭曲叶轮叶片完全适用不利起模工况条件下的生产。 关键词：常压消失模铸造；大扭曲叶轮；铸造工艺 中图分类号：TG249．6文献标识码：B 文章编号：1001—4977(201 1)12—1203—02 Application of Normal Pressure Lost FOam Casting to Big Warping Blade Wheel HE Li。ming (Dalian Deep Blue Pump Co．，Ltd．，Dalian 1 16031，Laioning，China) Abstract：The structural features and technological requirement of big blade wheel were analyzed， and the normal pressure lost foam casting process of blade wheel as well as the key points should be paid more attention to during the production were discussed．The result indicates that the normal pressure lost foam casting is suitable for production of castings like big warping blade wheel，which are difficult for paaern drawing． Key words：normal pressure lost f0am casting；big warping blade wheel；casting process 叶轮是泵的关键部件，叶轮的铸造技术和质量直 起模后的叶片形状，最终也就不能保证叶轮的水方I生能。 接影响着泵的水力性能、汽蚀性能及运行稳定性[I】。由 叶轮所用材质为304不锈钢，其化学成分为 (质量 于叶轮形状复杂，壁厚较小，采用常规的铸造方法根 分数)：≤0．08％C、≤2．0％Si、≤1．5％Mn、18．0％～ 本无法保证叶片的几何形状，自然也就保证不了泵的 21．0％ Cr、 ≤0．5％ Mo、8．0—11．0％ Ni、 ≤0．04％ P、 使用性能，若要保证叶片原状，生产中只有不进行叶 ≤0．04％S。 片起模。目前，多数生产厂通常采用常规的易熔合金 叶片进行生产，效率低、费用高。我公司将常压消失 2 常压消失模铸造的特点 模铸造工艺与传统砂型生产工艺相结合，解决了生产 (1)常压消失模铸造的造型制芯工艺与常规铸造 大型不能起模的大扭曲叶轮生产上的难题。 工艺基本相同。 消失模铸造与传统铸造的本质区别在于浇注时型