碳素原料种类对低碳镁碳材料结构与性能的影响.docVIP

碳素原料种类对低碳镁碳结构与性能的影响 摘要：研究不同种类的引入对镁碳结构与性能的影响。对镁碳的常温耐压强度、显气孔率、体积密度及抗氧化性进行检测，利用SEM对其显微结构进行表征。超细石墨作为的低碳镁碳其性能较优关键词：低碳镁碳 超细石墨 膨胀石墨 of different carbon on properties and structure of low-carbon MgO-C refractory Metallurgy Material Factory of Chongqing Iron Steel Group Mining Co., Ltd. DuChun-tian Abstract：The effect of different carbon on properties and structure of low-carbon MgO-C refractory was studied. Tests were made on the MgO-C specimens, such as cold compressive strength, porosity, volume density, room temperature thermal conductivity and anti-oxidation. Also the microstructure was characterized by SEM. The result shows that MgO-C refractory with ultra-fine graphite shows better performance and gets a compact structure, while the properties and structure of MgO-C refractory with carbon black is very bad . Key words: Low carbon MgO-C refractory, Carbon , Ultra-fine graphite, Expanded graphite 传统的镁碳［1］其10%～20%，随着冶炼技术对耐火材料的新要求，传统镁碳存在以下几方面的问题［2］：(1)高热导率增加热损耗，同时加大了耐火材料的侵蚀；(2)冶炼高质量洁净钢及超低碳钢时，会引起增碳问题；(3)消耗大量宝贵的石墨资源。因此，镁碳低碳化成为必然趋势。众所周之，镁碳中碳含量降低以后，使的热导率下降，弹性模量增大，从而使的抗热震性变差。另一方面，碳含量降低以后，使熔渣与材料的润湿性增强，材料的抗渗透性变差。 目前对解决这些问题的认识主要包括以下三个方面［3］：(1)通过改善结合碳的碳结构提高镁碳的热震稳定性； (2)优化镁碳的基质结构； (3)采用高效抗氧化剂。由于超细石墨［4～6］、炭黑、膨胀石墨［7、8］等碳素原料具有研究不同对低碳镁碳性能与结构的影响。1 试验过程 以电熔镁砂、天然鳞片石墨、超细石墨、炭黑和膨胀石墨为主要原料，以热固性酚醛树脂为结合剂200~300nm，比表面积为70m2 /g，膨胀石墨的膨胀容积约为200ml/g。将不添加碳素原料的参照试样编号为K组，其余各组分别添加3.5%的天然鳞片石墨、超细石墨、炭黑和膨胀石墨压制成Φ50mm×50mm圆柱状试样℃下干燥12h后，在匣钵中1000℃下进行埋炭处理。 1.2 性能测试 采用GB/T17732-2008致密定形含碳耐火制品试验方法，测定试样的显气孔率、体积密度、常温耐压强度和抗氧化性用对其显微结构进行表征。 2 结果与讨论 2.1图、图分别为的镁碳材料试样的体积密度和显气孔率，对比图（a）、(b)、（a）、（b），可以看出D2组试样无论是在220℃×12h还是1000℃×3h处理后，体积密度最大，相应的气孔率也最小，这是由于超细鳞片石墨粒度小，同时也容易分散，，，从而增大试样体积密度。以炭黑为碳，其粒度非常小，但易团聚不易分散，因此，气孔率最大，体积密度最小。 （a）220℃×12h干燥 b）1000℃×3h炭化处理 图试样体积密度 Fig of specimens （a）220℃×12h干燥 b）1000℃×3h炭化处理 图试样的Fig. 2 Apparent porosity of specimens 2.2常温耐压强度 图为的镁碳材料试样经干燥处理后和炭化处理后的常温耐压强度。分析）可知试样干燥处理后，D2组试样的常温耐压强度最高粒度小）1000℃炭化后，K组试样的常温耐压强度最高，其次为D2组试样。1000℃后当引入碳素原料，以超细鳞片石墨为碳源的D2组耐