掺入废旧橡胶颗粒及废旧聚氨酯颗粒对水泥砂浆性能的影响.pdfVIP

学兔兔 2014年第7期 混 凝 土 与水 泥 制 品 2014 No．7 7月 CHINA CONCRETE AND CEMENT PRODUCTS July 掺入废旧橡胶颗粒及废旧聚氨酯颗粒对 水泥砂浆性能的影响 徐 蕾，马青青 (新疆工程学院，乌鲁木齐830091) 摘 要：研究了掺入废旧橡胶颗粒及废旧聚氨酯颗粒的改性水泥砂浆的机械性能和导热系数。以体积比0．10％ 和30％的废旧橡胶颗粒及废旧聚氨酯颗粒代替石英砂配制出几种改性砂浆，通过试验检测了橡胶颗粒及聚氨酯颗 粒掺舍物对新拌砂浆的质量、抗压强度、抗弯强度和导热性能的影响，并通过掺加石灰石粉末作为填料得到最优化 的改性砂浆配比。结果表明，掺入橡胶颗粒及聚氨酯颗粒降低了材料的单位重量和导热系数，向时增强了隔热性能 关键词：水泥砂浆；橡胶颗粒：机械性能；导热系数 Abstract：The mechanical behaviour and thermal conductivity of cement mortar witll either sole rubber fSR1 or polyurethane(PU)waste particles are studied．Several mortar mixtures are prepared by replacing quartz sand with 0，10％， and 30％ of either SR or PU post-consumer plastic particles． rhe influences of SR particle or PU particle on the quality． compressive strength，flexural strength and thermal conductivity of the fresh mortar are tested．An optimization of mortar mixture proportions is carried out by adding a limestone powder as filler． rhe study results show that adding the rubber particles and PU particles in cement mortar can reduce both unit weight and the thermal conductivity of the raw mortar， and reinforce its theat—insulating property． ． Key words：Cement mortars；Rubber particles；Mechanical properties；Thermal conductivity 中图分类号：TU528．043 文献标示码：A 文章编号：1000—4637(2014)07—91—03 0 前言 轻质混凝土骨料已被成功应用于建筑物的各结构 随着能源消耗的日益严重．通过循环利用工业 中，对轻质混凝土的应用来说，结构的有效性比绝 和生活废料作为回收填料生产轻质复合材料，减少 对强度级别更为重要[71，对于同一强度而言，降低密 建筑使用中的能源消耗，同时解决环境问题成为倍 度将降低荷载、基础尺寸和建筑成本。 受关注的问题。目前采用的回收填料主要包括废玻 本研究通过掺人用废旧鞋底制成的橡胶颗粒 璃、粉煤灰、钢渣、轻质碎砖、橡胶颗粒、轻质膨胀黏 (Sole rubber，简称SR)及回收聚氨酯废弃物制成的 土骨料和聚苯乙烯泡’沫【”。其中，使用回收橡胶废料 废旧聚氨酯颗粒(Polyu