学兔兔 研究与应用 一 种反应粘结的新型防水卷材 游启明，曾东明，曾新龙 (广东科顺化工实业有限公司，广东 佛山 528303) 摘要：制备了一种反应粘结的新型防水卷材，通过对该卷材与后浇混凝土剥离强度影响因素的探讨，选定了主要原料及 其用量，并通过设计正交试验，优化了胶粘层配方。与普通粘结防水卷材相比，反应粘结型防水卷材与后浇混凝土间的 剥离强度更高，综合性能更优。 关键词：防水卷材；反应粘结；粘结机理；配方优化；制备 文章编号：1007—497X(2013)05—0020—04 中图分类号：TU57 3 文献标识码：A New Reactive Bonded Waterproofing Membrane You Qiming，Zeng Dongming，Zeng Xinlong (Guangdong Keshun Chemical Industry Co．，Ltd．，Foshan，Guangdong 528303，China) Abstract： New reactive bonded waterproofing membrane was prepared．The main materials and their dosages were determined by the analysis of the factors affecting the peel strength between the membrane and post—poured concrete．The formula of the adhesive layer of the membrane was optimized by orthogonal design．The reactive bonded waterproofing membrane had a higher peel strength and better comprehensive performance than that of common waterproofing membrane． Key words：waterproofing membrane；reactive bonding；bonding mechanism；formula optimization；preparation 普通自粘防水卷材与混凝土之间的粘结力主要 形成连续强力粘结，同时它能够与混凝凹凸表层形成 是分子间的范德华力(分子间作用力)，这种作用力属 物理卯榫结构，强化了这种粘结力，有效解决了上述 于附着力，键能只有2～20 kJ／mol，且只在自粘防水卷 自粘卷材因附着力不强所造成的空鼓、窜水等问题。 材中自粘层的分子与混凝土层的分子十分接近时才 1 卷材结构 会产生。然而，实际工程中，混凝土基面表层往往会存 反应粘结型防水卷材主要由HDPE、胶粘层、颗 在杂质及微观凹凸状态，部分自粘层的分子很难与混 粒层、隔离层构成，结构示意见图1。其中，胶粘层是 凝土基面分子接近产生分子问作用力，导致部分粘结 以SIS弹性体为主体的热熔胶，胶粘层中的活性剂能 失效。并且，已形成的附着力在受到热循环、水分子、 够与后浇混凝土发生反应，形成牢固的粘合；颗粒层 基层运动等作用力冲击时，也可能逐渐减弱，最终消 为无机硅氧化物，可充分填充混凝土表层凹陷空间， 失，导致粘结失效。本文介绍了一种新型防水卷材，该 形成卯榫结构；隔离层采用PET膜。 卷材通过化学键(键能60～700 kJ／too1)与后浇混凝土