钢中夹杂物去除与控制技术总结.pdfVIP

钢中夹杂物去除与控制 刘金刚 刘浏 （钢铁研究总院冶金工艺研究所，北京100081） 摘要：通过对钢包—中间包—结晶器中不同环节中的去除夹杂物的不同手段进行综合分 析，得到各环节中间包均应保护浇注和防止卷渣卷气，中间包应具有合理的结构（上下挡墙、 湍流抑制器、旋涡抑制器）以得到合理的流场；利用钢包注流的剪切破碎作用在中间包中生 成的小气泡、中间包气幕挡墙和电磁搅拌离心流动可以有效去除钢水中夹杂物；电磁制动技 术日趋成熟但其能耗较大，因此可以发展低能耗的中间包真空浇注对结晶器液面波动进行抑 制。电磁搅拌和电磁连铸有利于改善铸坯的内部质量和防止振痕的产生。 关键词：中间包 夹杂物 去除 控制 Inclusions Removal and Control in the Steel Melt Liu Jingang Liu Liu (CISRI, Beijing 100081) Abstract: Through synthetic analysis of various methods to remove inclusions during ladle-tundish-mold processes, it was found that using protective casting, avoiding gas and slag wrapping are important measures for clean steel production. The structure of the tundish should be reasonable, (dam, weir; turbulence inhibitor; vertex inhibitor) in order to get a preferred flow pattern. It could also utilize the shear flow from ladle to tundish to form small gas bubbles, utilize gas bubble curtain and electromagnetic stirring caused centrifugal flow to remove inclusions from steel melt. Electromagnetic braking technology is gradually raped but it was very energy consumed, thus it could develop low energy consumption vacuum tundish casting technology to control the fluctuation of melt surface in mold. Electromagnetic stirring is good for improving inner quality of slab and preventing the oscillation marks formation. Keywords: tundish, inclusion, remove, control 二○○三年我国钢产量已达到 2.7 亿吨，但由于质量问题一些高品质钢材仍需进口，这 已经成为我国钢铁工业发展的障碍，影响我国钢铁产品走向世界。钢质量问题也已经成为我 国由钢铁大国转变为钢铁强国的限制性环节，因此提高钢质量以增强国内钢铁企业的竞争力 十分重要。提高钢质量重点是提高钢的洁净度、对钢中夹杂物进行严格控制。 1 钢水脱氧与保护浇注 钢中夹杂物可分为内生和外来夹杂物，内生夹杂物主要是脱氧和合金化元素与溶解在钢 液中的氧以及硫、氮的反应产物所形成的夹杂物。外来夹杂物是钢液与空气、耐火材料、炉 渣及保护渣相互作用的产物以及机械卷入钢中的各种氧化物[1] 。因此提高钢质量必须通过控 制内生夹杂物和减小外来夹