YCZA30汽缸盖铸件顶面气孔成因及其对策.pdfVIP

学兔兔 材料与工艺 YCZA30汽缸盖铸件顶面气孑L成因及其对策 霍明新，杜文科，贾万军 (广西玉柴机器股份有限公司铸造厂，广西 玉林 537005) 摘要：通过对YCZA 30缸盖顶面气孔缺陷的成因进行分析，针对性地制定了防止措施。使用发气 量小的芯砂，防止整体浸涂过程中堵塞排气通道，以及使用砂芯替代铸型形成铸出孔的工艺， 能有效地解决缸盖类铸件的顶面气孔问题。 关键词：缸盖；气孔；宝珠覆膜砂；特种覆膜砂；呋喃树脂砂；整体浸涂 中图分类号：TG245 文献标识码：A 文章编号：1 673-3320(201 0)03—001 3—02 Prevention of Blowhole Defect on Top Surface of YCZA30 Cylinder Head Huo Mingxin，Du Wenke，Jia Wanjun (Found~Plant of Guangxi Yuchai Machinery Co．，Ltd．，Yu¨n 537005，Guangxi，China) Abastract：The reason causing blowhohe defect on the top surface of A30 cylinder head was analysed． and preventing pertinence measures were set down．The blowhohe defect on the top surface of cylinder head casting can be solved effectively by the process using core sand with low gas evolution，preventing exhausting channel from being jammed during holistic soaking and spreading，and replacing casting mold by sand core to form core hole． Key words：cylinder head；blowhole；pearl precoated sand；special precoated sand；furan resin sand； holistic soaking and spreading 玉柴机器股份有限公司铸造厂主要生产柴油 树脂砂射制生产，上下水套芯使用宝珠覆膜砂射 机发动机汽缸体和汽缸盖铸件，其中YCZA30柴油 制生产。全部砂芯组装后采用机械手整体浸涂工 机是我公司自主开发的6108系列增压机。A30汽缸 艺。组装砂芯前，需在上下水套芯芯头、进排气 盖为六缸机型，三缸一盖结构。在生产过程中，发 道芯芯头钻排气通道。砂芯组需经浸涂前芯组预 现顶面气孔废品率约4％，损失很大。为此本文对 烘烤和浸涂后芯组烘烤两次烘烤工艺，以确保砂 YCZA30汽缸盖顶面气孔缺陷的成因进行了深入的 芯水分符合工艺要求。 分析，并试图通过对YCZA30缸盖铸件项面气孔的 1．2．2 造型工艺 工艺改进，解决类似的缸盖铸件问题。 采用湿型黏土砂气冲造型，上外型局部喷涂。 1．2．3 熔 工艺 1 YCZA30缸盖结构及铸造工艺