ZG30MnSi中频炉熔炼工艺.pdfVIP

学兔兔 Sep．2011 铸 造 Vo1．60 NO．9 FOUNDRY ZG30MnSi中频炉熔炼工艺 陈 硕，闰永路，莫漓江 (三一重型装备有限公司，辽宁沈阳110027) 摘要：介绍了中频感应电炉熔炼ZG30MnSi工艺。通过对原材料质量的控制和化学成分的选择，及在终脱氧阶段， 对脱氧铝及钢液残余铝量的控制，获得了高质量的钢液，有效地减少了铸件出现气孔、夹渣等缺陷，细化了铸件的内 部组织，使铸件具有优良的综合力学性能，各项指标均超过国家标准。 关键词：中频感应电炉；ZG30MnSi；内部组织 中图分类号：TG243~．1 文献标识码：A 文章编号：100l一4977(201 1)09—0925—03 ZG30MnSi Melting Process with Medium Frequency lnduction Furnace CHEN Shuo，YAN Yong—lu，MO Li-jiang (SANYHE International Holdings Co．，Ltd．，Shenyang 1 10027，Liaoning，China) Abstract：The melting process for ZG3OMnSi with the medium frequency induction furnace was presented．Through measures such as the quality controI of raw materials．the selection of chemicaI composition．and the content controI of deoxidation aluminum and residuaI aluminum in molten steel in the finaI deoxidation stage．high—quality molten stee1 was obtained．The casting defects such as porosity。inclusions etc．were effectively reduced，and the internaI struIcture of the casting was refined．The casting has excellent mechanicaI properties．which are better than those of national standards． Key words：medium frequency induction fumace；ZG30MnSi；internaI structure ZG30MnSi中Mn、s冶量较高，正火后可获得较高 的强度和良好的塑韧性，因此，ZG30M】【lSi在工程机械 1 中频炉熔炼的特点 行业应用较为广泛。然而，对原材料控制不佳，在预 中频感应电炉作为熔炼合金钢的主要工具，具有 脱氧及终脱氧阶段，锰铁、硅铁加入顺序不正确及终 如下一些特点：①熔化效率高、节电效果好，结构紧 脱氧剂的种类、用量不当，会造成熔炼的ZG30MnSi钢 凑、过载能力大；②炉子周围温度低、烟尘少，作业 液含气量大、夹杂物多等不良后果，铸件的综合力学 环境好；③操作工艺简单，熔炼运行可靠；④金属成 性能达不到技术要求，见表1。为此，我们对 分均匀；⑤熔化升温陕、炉温容易控制，生产效率高； zG30Mnsi的熔炼工艺进行了研究，化学成分见表2， ⑥炉子利用率高