学兔兔 一 画 造型材料 挤压造型黏土湿型砂性能优化工艺 朱 筠 ， 、 伟 ，季敦生 (1．上海市机械制造工艺研究所有限公司，上海 200072；2．上海交通大学，上海 200240) 摘要：分析了挤压造型湿型砂黏结剂及附加物的性能特点，研究了优化添加剂对型砂性能的影 响，并进行了实际生产性试验。结果表明，采用型砂性能优化工艺，可稳定型砂性能，有利于 降低铸件表面的铸造缺陷率，提高铸件的品质。 关键词：黏土湿型砂；挤压造型；型砂工艺；优化添加剂 中图分类号：TG221 ．2 文献标识码：A 文章编号：1673-3320(2009)05-0006-03 Optimized Process of Green Sand Properties for Squeezing Molding ． ZhuYun ，Bo Wei ，Ji Dunsheng2 (1．Shanghai Institute ofMachine Building Technology Co．，Ltd．，Shanghai 200072，China； 2．Shanghai Jiaotong University,Shanghai 200240，China) Abstract：The characteristics of binder and additives for squeezing green molding sand were analyzed． The influence of the optimized additive on molding sand was studied，and the pouring test in production was performed．The results show that using the optimized process for molding sand can stabilize the sand performances，reduce the surface defects and improve the quality of castings． Key words：green molding sand；squeezing molding；sand process；optimized additive 采用高密度造型工艺生产的铸件不仅尺寸精 1 型砂黏结剂及附加物的分析 度高、表面粗糙度低，而且其组织致密、力学性能 1．1 膨润土 优，还具有生产效率高、劳动条件好等特点[I1。其中 高密度挤压造型湿型砂的特点是黏土含量 的挤压造型工艺不需使用砂箱，既节约了砂箱的材 高，水分含量低，所以作为型砂黏结剂一一膨润 料与工时费用，也简化了铸件落砂、清理等工序， 土的品质至关重要。若选用的膨润土性能差，将 尤其适合大批量铸铁件的流水线生产。高密度挤压 影响型砂的性能，从而导致铸件品质变差，也会 造型对型砂品质的要求比较严格，其型砂主要是由