71Q25.A356铝合金流变成形组织性能研究-北科崔建利.pdfVIP

2007 年全国塑性加工理论与新技术学术研讨会 2007 年5 月 沈阳 A356 铝合金流变成形组织性能研究 崔建利，康永林，徐 越 （北京科技大学材料科学与工程学院 100083 ） 摘 要：半固态加工技术被称为是21 世纪最有前途的加工工艺。本文以A356 铝合金为原料，在自行研制的新型半 固态浆料制备与直接流变成形设备上研究了A356 铝合金半固态流变成形组织性能随剪切速率，温度等工艺参数的变 化规律。 关键词：半固态； A356 ；流变成形；显微组织；力学性能 Study on Microstructures and Properties of Semi-solid A356 Alloy Produced by rheo-forming （University of science and technology, School of Materials science and Engineering , Beijing, 100083 ） Abstract: Semi-solid processing is the 21st century advancing front metal processing technology. In this paper, taking aluminum alloy A356 as trial material, and using the newly self-developed machine for preparing semi-solid slurry and direct fluidized forming as trial equipments, we study the changing principle of semi-solid microstructure and mechanical properties by changing the temperature and shearing rate. Key words: Semi-solid; A356; rheo-forming ;Microstructure; Mechanical properties 1 前言 为保护环境，节约能源，汽车发展的趋势是轻量化因此汽车的用铝量不断提高，但汽车对铝合 金零件（尤其是受力零件）的要求严格，世界各国都在不断研究探索铝合金汽车零件毛坯的制造新 技术、新工艺，铝合金半固态成形技术便是其中之一。利用半固态铝合金成形技术可以生产出高致 密性（即高可靠性）的近终形化的汽车零件毛坯，因此铝合金半固态成形技术的应用，对促进国民 经济的发展和环境保护都具有重大的意义。 A356 合金属于Al-Si 系多元合金，其流动性和铸型的填充性好，具有优良的铸造性能，该合金 制作的铸件可获得较高的强度和延伸率，也有较好的抗氧化和耐腐蚀能力，密度小、热膨胀系数小， 并具有高抗冲击性和高压下的致密性。因此，A356 铝合金目前被广泛应用于汽车、摩托车、航空航 天工业以及家用电器等产品的制造中，是一种很有发展前途的铝合金。[1,2] 本文采用独立开发的转筒式半固态流变成形设备，主要研究了通过机械搅拌下半固态浆料流变成 形，来改善 A356 合金的组织和性能，并研究了半固态组织和性能随温度和剪切速率等工艺参数的 变化规律。 2 试验材料、设备及方法 2.1 试验材料与试验设备 表1 A356 铝合金的化学成分（wt% ） Si Fe Cu Mn Mg Zn Ti Cr Ni Sn Al 6.93 0.17 0.01 0.01 0.38 0.01 0.15 0.05 0.05 0.01 balanced 389 2007 年全国塑性加工理论与新技术学术研讨会