制药机械用钢材制造前的腐蚀与防护.PDFVIP

·78· 维修与改造 机械 2005年第4期总第32卷 制药机械用钢材制造前的腐蚀与防护 雷吉平 （长沙正中药机厂，湖南长沙 410006 ） 摘要：为了降低制药机械用钢材制造前由于防护不当所造成严重的腐蚀，在很大程度上保持钢材应具有的使用价值，对 制药机械用钢材制造前的维护过程中的腐蚀机理进行了详尽研究，并提出了一些合理性的防护措施。结果表明：制药机 械用钢材的腐蚀率大大降低。 关键词：钢材；腐蚀；防护；制药机械 中图分类号： TG142.1 文献标识码：B 文章编号：1006－0316(2005)04－0078－03 Corrosion and defending on steel being used for pharmaceulical machine LEI Ji-ping （Changsha Zhengzhong pharmaceulical machine factory，Changsha 410006 ，China ） Abstract: In order to reduce serious corrosion on steel being used for pharmaceulical machine based on unsuited defending and keep its use value in a very degree, the corrosion mechanism steel being used for pharmaceulical machine was studied strictly in the defending course, and some reasonable defending measures were given. The results revealed that the corrosion rate of steel being used for pharmaceulical machine had been reduced in a very big degree. Key words: steel plate；corrosion resistance；galvanization；pharmaceulical machine 钢材是制造制药机械的主要原材料之一，优良 钢材在干燥气体或无电解质存在的环境中，受 的钢材若保护不当，将会在不太长的时间内造成严 氧化物质的直接作用，而过程中不产生电流的腐蚀 重的腐蚀，从而在很大程度上降低钢材应具有的使 现象叫化学腐蚀。例如：钢材在常温干燥环境中， 用价值。对于处于雨水浸蚀、工业区的大气腐蚀、 受 SO 、CO 、O 、H 等气体的作用，以及在非电 2 2 2 2 沿海地区氯化钠的浸蚀等环境中的制药机械厂家， 解质液体(如汽油、润滑油) 中所引起的腐蚀现象，都 此问题尤其值得引起重视。近年来人们对金属大气 是化学腐蚀。 [1-5] 腐蚀 的研究较多，但对在大气条件下环境因素钢 1.2 电化学腐蚀 材制造前的腐蚀与防护的研究却较少。本文就制药 机械用钢材制造前的腐蚀与防护作一些简单介绍。 钢材在电解质中，由于各部位电位不同，产生 微电池，在电子交换过程中产生电流，作为负极的 1 钢材腐蚀的机理 金属逐渐被溶解，导致钢材腐蚀，日常大量钢材的