浅析膨胀玻化微珠砂浆外保温层脱落原因及防治措施.docVIP

浅析膨胀玻化微珠砂浆外保温层脱落原因及防治措施 　　【摘要】外墙外保温是当前建筑节能的重大措施，针对外墙外保温体系自身的特点，本论文紧密结合工程案例，着重从人、机、料、法、环等5个方面，全面分析了无机膨胀玻化微珠保温砂浆外墙保温层产生脱落的原因，根据原因制定了相应的防治措施 【关键词】外墙保温；脱落；原因；措施 Analysis on the Cause of Exfoliation of Externally Insulating Layer of Expanded and Vitrified Microsphere Mortar and Preventive Measures Feng Wen-cheng （Shanghai Railway Real Estate Development Management Co.， LtdShanghai200071） 【Abstract】n view of the characteristics of the external thermal insulation system， this paper， combined with the engineering case， focuses on five aspects， such as man， machine， material， method and ring， The causes of the shedding of the thermal insulation layer of the vitrified microsphere thermal insulation mortar and the corresponding prevention and control measures were formulated according to the reasons. 【Key words】External wall insulation；Loss；Reason；Measures 1. 引言 目前，民用商品住宅外墙已普遍采用外墙保温系统，不仅可以提高房屋建筑的耐久性，延长建筑物的使用寿命，还可以改善居住条件，起到隔热保温减少能量消耗的作用，是建筑节能环保中的重要一环[1]。外墙外保?夭愕耐崖洳唤龃嬖谧叛现氐陌踩?隐患，还影响小区建筑的整体品质，甚至有损于企业的品牌形象，造成负面的社会影响。因此，采取有效举措防治外墙外保温层脱落具有重要的现实意义和经济社会效益 2. 外墙保温层工程案例分析 2.1工程概况 XXX住宅项目是保障性住房工程，为框架剪力墙结构。该工程建筑总面积115584m2，其中包括了24～32层的七栋单体建筑，建筑最高94.6m，最低的高度69.75m。外墙外保温层面积共约101695m2，保温层厚度35mm，真石漆涂料饰面，保温材料采用了无机膨胀玻化微珠保温砂浆 2.2无机膨胀玻化微珠砂浆外墙保温系统分析 该工程项目所采用的无机膨胀玻化微珠砂浆外墙外保温系统具体做法为：保温层由无机玻化微珠保温砂浆加水搅拌后，抹于墙体表面，形成无空鼓保温层。抗裂砂浆、耐碱玻纤网格布（涂料饰面）构成抗裂防护层，抗裂防护层增强了面层柔性变形、抗裂防水性能。该外保温结构体系自内向外为：界面砂浆→保温砂浆→抗裂砂浆（压入耐碱玻纤网格布）→柔性耐水腻子→面层涂料+罩面涂膜。如图1 3. 无机膨胀玻化微珠砂浆外墙保温层脱落原因分析 该项目先期施工的一标段1#、2#楼工程，其中1#楼西侧外墙的保温层在30层窗户与墙面结合部，出现约5m2的开裂空鼓，2#楼25层外墙北立面与东立面保温层的结合处，出现约7m2的开裂空鼓而引起保温层脱落，重点从人、机、料、法、环等5个方面进行原因分析 3.1材料方面。保温材料没有根据施工现场的具体条件进行材料配比优化，如当时的环境温度、湿度和保温层的厚度等，使得保温砂浆的保水性、抗拉强度等性能不能满足工程要求而引起开裂空鼓；材料纤维成分含量较少或材料品质的问题导致保温砂浆保水效果不好，使砂浆中的水分自由流动从而形成空鼓；掺加剂中的高分子改性组分没有充分考虑施工温度和胶凝材料的强碱性等因素的影响，未能充分溶解，造成保水性和抗拉强度未达要求 3.2机械方面。保温砂浆搅拌不均匀，浆料的和易性不佳；施工搅拌机械设备数量不够，无法满足施工需要，从而部分浆料采用人工搅拌，保温砂浆上墙后部分位置含水量过高，造成浆料内部水分流动，在保温层终凝后形成开裂和空鼓；在搅拌过程中，缩短搅拌时间使浆料均匀性得不到保证，而外加剂、胶粉料等改性组成部分未能够充分溶解，造成成型砂浆的粘结性不够 3.3施工人员方面。由于保温层施工人员的针对性培训不够，