JMEPEG ASM International DOI: 10.1007/s11665-013-0519-x 1059-9495/$19.00 Evaluation of Cu-Zr-Ti-In Bulk Metallic Glasses via Nanoindentation J.L. Wu, Y. Pan, and J.H. Pi (Submitted December 6, 2012; in revised form February 18, 2013) In this paper, the mechanical properties of two bulk metallic glasses, Cu Zr Ti In and Cu Zr Ti In , 60 34 5 1 58 34 5 3 have been evaluated by nanoindentation tests. The hardness and Youngs modulus of as-cast Cu60Zr34- Ti In bulk metallic glass increase from the center to the edge of the rod, but Cu Zr Ti In shows an 5 1 58 34 5 3 inverse trend. The Youngs modulus of Cu Zr Ti In is lower than that of Cu Zr Ti In . For both bulk 58 34 5 3 60 34 5 1 metallic glasses, serrations on the nanoindentation load-displacement curves depend not only on loading rate but also on the maximum load. Alternatively, the onset position of the appearance of serrations on the curves increases with the loading rate. In addition, the hardness of both samples decreases as the size of the indent increases due to indentation size effects.