得普乐 （DAPOL） 乙二酸酞脂（零本二甲酸已二烯酯）树脂成形材料 Diallyl Phthalate Molding Compounds 试验项目TEST ITEMS 单位 UNITS 试验办法 TEST D500 D2500F D2200F 绝缘破坏的强度 Dielecttic breakdown sttength 常温状态 at oedinary state MV/m JIS K6911 12-16 12-16 12-14 浸泡后 after immersion in water 12-16 - - 绝缘电阻 Insulation resistance 常温状态 at oedinary state Ω JIS K6911 1014-1015 1014-1015 1014-1015 沸腾状态 after boiling 1013-1014 1013-1015 1013-1014 长期湿中电气电阻 Insulation resistance after Moisture treatment for long time 体积 volume Ω JIS K6918 109-1010 - - 表面surface 108-1010 - - 电容率（1MHz） Dissipation constant 常温状态 at oedinary state - JIS K6911 4.4-4.6 4.3-4.6 4.3-4.6 浸泡后 after immersion in water 4.4-4.7 - - 感应电正切（1MHz） Dissipation Factor 常温状态 at oedinary state - JIS K6911 0.012-0.015 0.010-0.015 0.010-0.015 浸泡后 after immersion in water 0.012-0.017 - - 耐狐光性 Arc resistance S JIS K6911 120 130 160 变成导电体的几率低性 Tracking resistance CTI(V) IEC 112 500 500 500 弯曲强度 Flexural strength 射出成形 Injection molding Mpa (kgf/mm2) JIS K6911 98-147 10-15 78-137 8-14 127-147 13-15 压缩成形Compression molding Mpa (kgf/mm2) 69-98 7-10 69-98 7-10 - - 冲击强度 Charpy impact sttength 射出成形 Injection molding KJ/m2 (kgf.cm/c m2) JIS K6911 3.4-5.4 3.5-5.5 3.4-5.4 3.5-5.5 3.9-5.9 4.0-6.0 压缩成形Compression molding KJ/m2 (kgf.cm/c m2) 2.9-4.9 3-5 2.9-4.9 3-5 - - 成形收缩率 Molding Shrinkage 射出成形 Injection molding ℅ JIS K6911 0.5-0.8 0.6-0.8 0.4-0.6 压缩成形Compression molding 0.4-0.7 0.4-0.6 - 高温尺寸变化率 Rate of shrinkage on heating ℅ JIS K6918 0.05-0.10 0.05-0.10 0.05-0.10 加热后的外观 Appearance after heating ℃.2h JIS K6911 180 180 280 负荷量挠曲的温度Deflection temperature under load ℃ JIS K6911 170-180 160-180 280-300 耐燃性 Flammability - UL94 94HB (1.02) 94V-O (1.02) 94V-O (0.50) 沸腾吸水率 Boiling water absorption ℅ JIS K6911 0.15-0.25 0.10-0.20 0.10-0.15 比重 Specific gravity - JIS K6911 1.60-1.70 1.80-1.90 1.85-1.90 成形办法 Molding method 射出，移送，压缩 射出，移送 其他特性 Others properties 增大系数 Bulk factor 2.3 JIS K6915符合记号 种类 Types 电气，电子用For hight polencial insulation 耐燃用