钢箱梁桥铺装用环氧沥青材料制备和表征.pdfVIP

Journal of Southeast University ( English Edition) Vol. 22 , No. 4 , pp . 553 - 558 Dec. 2006 ISSN 1003—7985 Preparation and characterization of epoxy asphalt binder for pavement of steel deck bridge 1 1 2 2 Chen Zhiming Kang Yang Min Zhaohui Huang Wei ( 1 School of Chemistry and Chemical Engineering, Southeast University, Nanjing 210096, China) ( 2 School of Transportation, Southeast University, Nanjing 210096, China) Abstract: A kind of thermosetting asphalt binder designated as epoxy asphalt, which is composed of two components: maleated asphalt with curing agents and accelerant of epoxy resin and epoxy resin, was prepared. Its paving feasibility and concrete performances were investigated using Brookfield viscosimeter, direct tensile test ( DTT) , Marshall testing and the MTS 810 hydraulic servos-system, respectively. Although only 50% to 60% of added maleic anhydride ( MAH) reacted with the base asphalt irreversibly ( probably by Diels-Alder mechanism) , the curing rate, rupture elongation and tensile strength of maleated epoxy asphalt were enhanced more evidently than those of unmaleated epoxy asphalt . As a result, an epoxy asphalt made from 4% MAH modified asphalt and other curing agents was featured to have an average rupture elongation of 281. 9% , an average tensile strength of 2. 63 MPa, and the Marshall stability of its cured concrete reached 37. 0 kN, while that of uncured concrete was 10. 2 kN and the combined beam o