钢筋电渣压力焊工艺标准(国外英文资料).docVIP

钢筋电渣压力焊工艺标准(国外英文资料) Welding technology standard for steel and steel slag 1 scope The technology standard is applicable to industrial and civil building cast-in-place reinforced concrete structure in 14-40 mm diameter class I - Ⅱ vertical or inclined The connection of the steel bar to (the slope of 4:1). 2 construction preparation Materials and main tools: Steel bar: the level of the steel bar, the diameter must meet the design requirement, have the factory certificate and the retry report form. Import of steel bar should also be The chemical composition should meet the welding requirements and should be tested for weldability. 2.1.2 flux The performance of 2.1.2.1 flux shall conform to the stipulations of GB5293 carbon steel submerged arc welding flux. The solder type is HJ401, commonly used Smelting type high manganese high silicon low fluoride flux or medium manganese high silicon low fluoride flux. 2.1.2.2 flux should be stored in dry storage room to prevent moisture. If be affected with damp be affected with damp, before use must be approved by 250-300 ℃ for 2 h. 2.1.2.3 shall be used for the removal of slag and sundries, and shall be used after mixing with the new flux. 2.1.2.4 solder should be given the factory certificate. Main machine tools The welding equipment including welding power supply, control box, welding fixture, flux can etc. 2.1.3.2 automatic electroslag pressure welding equipment (should be adopted first) including: welding power supply, control box, operating box, welding head etc. 2.1.3.3 welding power supply. It is advisable to use the secondary light load voltage (TSV above) for ac or dc welding The source. (32mm diameter and the following bar welding, can be used for welding power supply of 600A; 32mm diameter and above steel When the reinforcement is welded, the power supply should be made of 1000A. When the welders capacity is more than an hour, the same model can be used for smaller size The two welders of performance are used in paralle