りん光有機EL素子の効率耐久性向上技術開発.PDF

UDC 621.382＋621.3.032.35＋544.523 りん光有機EL素子の効率・耐久性向上技術開発 ＊ ＊ ＊ ＊ 外山　弥 ，佐藤　祐 ，木下　正兒 ，飛世　学 ， ＊＊ ＊＊＊ ＊＊＊ ＊ 河戸　孝二 ，伊勢　俊大 ，滝沢　裕雄 ，山下　清司 Development of efficiency and stability of phosphorescent organic electroluminescent devices Wataru SOTOYAMA*, Tasuku SATOH*, Masaru KINOSHITA*, Manabu TOBISE*, Kouji KAWATO**, Toshihiro ISE***, Hiroo TAKIZAWA***, and Seiji YAMASHITA* Abstract We developed stable and efficient blue phosphorescent materials for organic electroluminescent (EL) devices on the basis of the evaluation of their stability under UV irradiation. Structures of organic EL devices with the above-stated materials were improved with the aid of a method to estimate the site distribution of exciton formation in the emissive layer by doping it with a small amount of fluorophore at varied positions. The improved blue phosphorescent organic EL devices showed high external quantum efficiency (7.9%) with a half life of 10,000h at a practical luminance (360 cd/m2). 1. はじめに 　自発光，高速応答，薄型軽量などの優れた特徴を持つ 有機エレクトロルミネッセンス（EL）素子は，携帯端 末や小型テレビ用ディスプレイとしての実用化が始ま り，照明光源への適用も期待されている。 　有機EL素子は，2つの平板電極で厚さ100nmオーダー の有機薄膜を挟んだ構造を持つ。その発光メカニズムは 無機半導体LEDに類似しており，電極から注入された 正孔と電子がそれぞれの輸送層を通って発光層に注入さ れ，再結合により分子の励起状態（励起子）が生成して Fig. 1 Structure of a typical organic EL device. 発光が起こる（Fig. 1）。このとき生成する励起子は，正 孔と電子のスピンのランダムな組み合わせにより，25％ が一重項励起子，75％が三重項励起子として生じるとさ 　一方三重項励起子からの発光を利用するりん光EL素 れている。このため一重項励起子からの発光を利用する 子では，再結合で生じた75％の三重項励起