基于废旧涤纶纺织品再生聚酯降解流变行为探究.docVIP

基于废旧涤纶纺织品再生聚酯降解流变行为探究 　　摘要：以废旧涤纶纺织品再生聚酯和原生聚酯为原料，采用Rosand RH-7型毛细管流变仪对其降解流变行为进行研究。结果表明：一定温度下降解处理后，再生聚酯和原生聚酯仍表现出典型的假塑性流动行为；与原生聚酯相比，一定温度范围内，再生聚酯在较低的温度下即开始发生降解，且降解主要发生在降解处理的前 5 min；随着剪切速率的提高或者停留时间的延长，2 种聚酯的△Eη均呈下降的趋势，但再生聚酯的△Eη均略大于原生聚酯的△Eη；与原生聚酯相比，再生聚酯的结构粘度指数均较大，预示再生聚酯在熔纺加工时可纺性较差 关键词：废旧涤纶纺织品；再生聚酯；降解流变行为；粘流活化能；结构粘度指数 中图分类号：TQ342.21 文献标志码：A A Study on the Degradation-rheological Behavior of PET Regenerated from Used Polyester Textiles Abstract： TPET regenerated from used polyester textiles and native polyester were used as raw materials and their respective degradation-rheological behavior was studied by using Rosand RH-7 capillary rheometer. The results showed that after the degradation process at certain temperature， both materials showed a typical pseudoplastic flow behavior. Compared with native polyester， the regenerated polyester started degrading at a lower temperature， and the degradation occurred mainly within the first 5 min. of the degradation process. With the increase of shear rate or the retention time of the degradation treatment， the△Eη of both polyesters was found decreasing. Compared with the native polyester， the structural viscosity index of the regenerated polyester was relatively higher， predicting that the regenerated polyester would exhibit poor spinnability in the melt spinning process. Key words： waste polyester textiles； regenerated polyester； degradation-rheological behavior； flow activation energy； structural viscosity index 本研究以由废旧涤纶纺织品（军装）经醇解再聚合得到的再生聚酯切片为原料，利用毛细管流变仪考察其在不同降解条件下的流变行为，并与直接由PTA和EG聚合得到的聚酯切片（简称“原生聚酯”）进行对比，以期为由废纺所得再生聚酯的纺丝工艺优化与精准控制提供基础数据 1 实验 1.1 原料 再生聚酯切片：浙江富源再生资源有限公司，由废旧涤纶军装经醇解、液相增粘所得，特性粘数0.684 dL/g；原生聚酯切片：天津石化有限公司，膜级大有光切片，特性粘数0.670 dL/g 1.2 测试与表征 1.2.1 降解流变行为测试 仪器：Malven公司Rosand RH-7型毛细管流变仪；测试条件：采用材料降解模式毛细管长径比16/1，毛细管直径0.5 mm，剪切速率（）2 000 ～ 10 000 s-1，降解时间（用样品在料筒内的停留时间表示）分别为 0、5、10 min，再生聚酯测试温度280、285、290、295 ℃，原生聚酯测试温度285、290、295、300 ℃；测试方法：将经真空干燥箱充分干燥的 2 种聚酯切片放入已设置好测试条件并达到设置温度的流变仪料筒中，开始测试得到不同条件下的流