微合金管线钢X70控制轧制与控制冷却工艺的研究.pdfVIP

鞍山科技大学硕士论支 TheStudyofControlledRollingandControlledCooling ProcessonMicro-alloyedPipelineSteelX70 Abstract Pipelinesteelsplayanimportantroleinthedevelopmentofnational economy.Ithasrealisticsignificanceandvaluetoresearchanddevelophigh properlypipelinesteel. The controlled rolling and controlled cooling technology isvery importantinmodernsteelproducts.Thispaper,applycontrolledrollingand controlledcoolingtechnologyontheproductionofmicro-alloyedpipeline steelX70,studytheeffectofthistechnologyontransformationand microstructureofpipelinesteelX70andtheeffectofcoolingrateafter deformationontransformationandmicrostructure.Theexperimentswere madeattheGleeble-1500thermo-mechanicalsimulator.Themaincontents aregivenasfollows: I.ThehardnessanddynamicrecoveryofX70duringhotdeformationwere investigatedbysinglepasscompressiontest.Thestaticrecrystallization actionofthissteelduringtheintervaltimeofdeformationwasstudiedby two-passcompressiontest. 2.Studytheeffectofdeformationconditionsonaustenitetransformation behaviorandferrite refinementbydifferentpasscompressionand deformation. 3.Studytheeffectofcoolingrateondeformationferritemicrostructureby meansofdifferentcoolingrateofdeformedsamples. 4.Studytheeffectofsoakingtimeonaustenitetransformationbehaviorand microstructureofmicro-alloyedpipelinesteelX70bytwopasscompression test.Providereasonablereferenceforproduction. Keywords:Micro-alloyedpipelinesteel,Controlledrolling,Controlledcooling, Microstructure,Transformation 11 鞍山科技大学硕士论文 第一章 综述 第一章 综 述 前言 管线钢是热轧带钢产品的重要品种之一。它主要用于石油、天然气等 的管道运输方面，在国民经济中占有举足轻重的地位 。特别是近年来由于 我国石油开采向西部转移，新设计的管线采用常温、长距离输送方式，输 送 扭力也相应提 高，加之管线要跨越许 多江 、河 和地 质断裂带 ，从而对钢 的强度和韧性提出了更高的要求，因此高强度、高韧性管线铜的研制与开 发己成为当今A.待解决的问题之一’【〕。同时，伴随着西部大开发的深入发 展，西部的巨大的能源资源已被人们发觉。它蕴藏着的丰富的天