　　　　　　　　　　　　　　　　　　　　阀　　　门　　　　　　　　　　　　　　　2007 年第 4 期 —34 — 文章编号 : (2007) 热风阀阀板的长寿化探讨 1 2 1 马学东 , 宋兆峰 , 李玲玲 (1 辽宁科技大学 , 辽宁 鞍山 114044 ; 2 秦皇岛冶金机械有限公司 , 河北 秦皇岛 066004) 　　摘要 　针对国内热风阀阀板外水环经常出现裂纹的实际情况 , 运用有限元方法对热风阀阀板 的温度场和热应力场进行了分析 , 其结论为热疲劳是引起裂纹的重要原因之一 , 并提出了防止热 疲劳的措施 。 　　关键词 　热风阀; 阀板 ; 长寿化 　　中图分类号 : TH134 　　　　文献标识码 : B Longevity discussion of valve plank of hot blast valve MA Xuedong1 , SON G Zhaofeng2 , L I Lingling1 ( 1. University of Science and technology Anshan , anshan 114044 , china ; 2. Qinhuangdao Metallurgical Machinery Co. , L TD , Qinhuangdao 066004 , China) Abstract : Aimed at practical circumstance that crack often appears on outer water loop of valve plank for existing hot blast valve in our country , making use of finite element method , temperature field and thermal stress field of valve plank for hot blast valve is analyzed. And it draws a conclusion that heat fatigue is one of important reasons which gives rise to crack and brings forward some measures which prevents heat fatigue. And all that provides theoretical reference for longevity of hot blast valve. Key words : hot blast valve ; valve plank ; longevity 1 　概述 热风阀阀板使用温度为 1 000～1 350 ℃, 必须 通过冷却才能正常工作 。在热风阀的各个构件中 , 常因阀板外水环出现裂纹而引起整个设备出现故 障 , 制约了热风阀的产品质量提高和设备使用寿命 1 内水环 　2 钢质骨架 　3 耐火水泥衬 　4 外水环 的延长 。本文采用大型有限元软件包 ANSYS 对国 图 1 　阀板几何模型 内某钢厂的热风阀阀板温度场和热应力场进行数值 2 2 　有限元模型 模拟 , 并根据模拟结果对阀板的使用维护提出了建