74丘克强 氧化锌反应合成纳米硫化锌粒度变化机制-2.pdfVIP

氧化锌和硫化钠反应合成制备纳米硫化锌的粒度变化机制1 丘克强, 龙桂花，曾恒志 （中南大学化学化工学院冶金及应用物理化学研究所长沙 410083 ） 摘要：在超声波作用下，我们利用氧化锌粉和硫化钠溶液反应制备出了纳米硫化锌。本文对 该方法制备纳米ZnS颗粒的粒度变化机制开展研究，实验结果表明：ZnS粒度随着反应温度 的提高及液固比的增加逐渐增大；随反应时间的延长，先增大后减小；随Na2S摩尔浓度的 增加而减小；随超声波的加入，颗粒粒度显著变小，并且能够达到纳米量级；没有超声波作 用所形成的ZnS颗粒只能达到微米量级。 关键词：超声波；氧化锌；纳米硫化锌；结晶。 中图分类号：O614.24 Mechanism of the particle size change of Nanoparticles ZnS prepared by solid-liquid reaction of ZnO and Na S 2 QIU Ke-Qiang , Long gui-hua , ZENG Heng-Zhi (College of Chemistry and Chemical Engineering, Central South University, Hunan, Changsha 410083,China) Abstract ：Nanoparticles ZnS were prepared with ZnO and Na S by solid-liquid chemical reaction 2 under ultrasonic condition. Mechanism of the particle size change of Nanoparticles ZnS was investigated in this work. The results show that the particle size of ZnS gradually augments along with the increase of the reaction temperature and liquid-to-solid ratio,while with the increase of the reaction time, it augments first and then reduces, and reduces with the increase of the molar concentration of Na2S. With the addition of ultrasound, the particle size of ZnS decreases significantly and can achieve the nanometer magnitude, otherwise only micron magnitude. 纳米微粒是指粒度为纳米量级（1~100nm）的超细微粒。当粒子尺寸达到纳米量级时， 其本身具有量子尺寸效应、小尺寸效应、表面效应和宏观量子隧道效应，因而在催化、非线 性光学、磁性材料、医药及新材料等方面有广阔的应用前景[1] 。作为一种过渡金属硫化物， 纳米硫化锌显示出许多特异的光电性能，它的电致发光和光致发光效率较高[2,3]，在光致发 [4-6] 光、电致发光、磷光体、传感器、红外窗口材料、光催化等许多领域有着广泛的用途 。 因此，制备具有特定形态、粒度小并且可控的硫化锌颗粒显得十分重要，并成为了近年的研 究热[7-22]，而制备的方法可分为物理法和化学法两大类，其中物理方法主要有：气相沉积法、 溅射沉积法、低温等离子法和蒸汽冷凝法等；化学法主要有水热溶剂热法、化学沉淀法、微 乳液法、溶胶凝胶法和LB膜法等，但是用这些方法制备粒径发布窄的 硫化锌纳米粒子仍有 很大的难度，因此制备粒径可调、发布较窄的 纳米硫化锌仍然是我们面临的重要课题。最 近，我们成功开发了在超声波