渗碳淬火件表面层非马氏体组织形成的原因和防止-重庆义扬机电设备.DOCVIP

再述：渗碳淬火件表面层非马氏体组织形成的原因和防止措施 （怎样使渗碳表面层质量处于世界领先地位，同时节能、降耗、经济效益可观） 李志义1，2，马学文3，蒲 玲4，，向书胜5,李晓澎1，2 （1.重庆义扬机电设备有限公司,重庆 400039; 2.重庆长江工业炉公司, 重庆 401329; 3.株州齿轮公司,湖南 株州 400029; 4.四川丹齿实业公司,四川 丹陵 612260; 5.重庆建设工业集团有限公司, 重庆 400050) 摘 要: 在《金属热处理》2000年第25卷第11期刊登题为“渗碳淬火件表面层非马氏体组织形成的原因和防止措施”和在《齿轮传动》2011.(6)：79-86刊登题为：再述：渗碳淬火件表面层非马氏体组织形成原因和防止措施的基础上，依据近壹年在热处理生产中的实际总结和产品质量的检验，对渗碳淬火件表面层非马氏体组织形成的原因和防止措施有了新的见解并加以完善。再次强调了采用净化后的天然气、甲醇、氨气等渗碳气源是减少非马氏体组织的重要措施，并且在检查非马氏体组织时一定要浅腐蚀、晶间氧化（不腐蚀）2011年5月北京三一重工（艾协林多用炉）姚东海首先发现：在风电、重载齿轮渗碳上有效硬化层2.5～3mm，晶间氧化（不腐蚀）15～20μm。表面层质量处于世界领先地位（2011年8月重庆新兴通用丰东韩伯群总工也发现类似效果）。 关键词：非马氏体组织；气源净化；浅腐蚀 Further Discussion on the Forming Reasons of Non-martensite Structure on the Surface Layers of Carburized and Quench Hardened Parts and Its Preventive Measures ( how to make the quality of carburized layer in a leading position in the world, at the same time, energy saving, consumption reduction, substantial economic benefits ) Li Zhiyi1，2, Ma Xuewen3, Pu Ling4, Xiang Shucheng5, Li Xiaopeng1，2 Abstract: In the metal heat treatment in 2000 twenty-fifth volume eleventh periodical published entitled the hardened steel surface layer of martensite formation reason and prevention measures and in gear 2011 ( 6) : 79-86 published entitled: the: carburizing quenching surface layer of martensite formation reason and prevention measures on the basis, according to the recent one year in heat treatment production in the actual sum and product quality inspection, carburization and quenching, surface layer of martensite formation reason and prevention measures in a new light and sound. Once again stressed the importance of using purified natural gas, methanol, ammonia carburizing gas source is to reduce the martensite are important measures, and in the examination of Non-martensitic structure must be superficial corrosion, intergranular oxidation ( corrosion ) in 2011 May Beijing Sany ( Ai Xielin furnace ): Yao Donghai first discovered in wind power, heavy-duty gear carburizing on the