非织造机织pet和纺粘pp的混杂复合材料的制作性能检测大学论文.docVIP

机织PET和纺粘PP混杂复合材料的制备及性能检测 摘要 Mpa，层压时间是10min。 关键词：复合材料；热塑性聚合物；有机纤维；性能测试 PET mixing with spun-bonded PP woven composites Preparation and performance test Abstract At present, the development of composite materials with each passing day, the study of various composite materials also made great progress, but for the research of fiber reinforced composites or weaknesses. Is against this background this paper chose the organic fiber and thermoplastic polymer composite materials for research. This design mainly by the more compared with typical woven PET spun-bonded PP hybrid composite material preparation and testing to complete the study of its performance. Compared to other materials, a woven materials chosen for the experiment, a spun-bonded nonwoven materials, can better improve the students professional knowledge. This experiment mainly through for woven PET and spun-bonded PP woven with hybrid composites in the body of PET and the change of the mass fraction of spun-bonded PP and through to the fixed ratio enhanced body woven PET and PP spun-bonded different layer in order to the preparation of the test sample, and used for performance testing, and woven PET and PP spun-bonded proportion of the best preparation of composite materials. Through the comprehensive data analysis to test whether there is compared to a single composite material superiority, will be able to achieve some performance of the single material does not have. Laminated over each group sets up three samples, optimize the main working procedure, to determine the optimal process parameters. Laminating the selected process conditions: temperature is 135 ℃, pressure is 3 Mpa, laminated time is 10 min. Key words； composite material， Thermoplastic polymer； Organic fiber； The performance test 目录 引言 1 第1章 绪论 2 1.1 机织PET和纺粘PP混杂复合材料的意义 2 1.2 在国内外目前对此研究的现状 2 1.3 研究内容 3 第2章 原材料的基本性质及实验材料的制备过程 5 2.1 原材料的基本性质 5 2.1.1 机织PET的基本性质 5 2.1.2 纺粘PP的基本性质 5 2.1.3 LDPE膜的基本性质 6 2.2 实验材料的制备过程 6 2.2.1 实验方案的设