两化考试题库(国外英语资料).doc

两化考试题库 Standardized training examination questions of three major regulations I. judgment questions (80 questions) The desulfurization capacity of CaC2 is stronger than that of CaO. (V) Alkalinity is the only sign of slag removal of P and S capacity. (x) CO are colorless, tasteless, poisonous and explosive gases. (V) PPM means 1/10000. (x) Variable gun operation means that the gun position is high in early stage and lower in middle and later stage. (x) The recovery of manganese in tapping is higher than that of silicon. (V) After tapping, the temperature of molten steel is too high to cool down with scrap scrap. (V) The main reason for tapping P back is that adding deoxidizer to steel during the tapping process reduces the [O] and (FeO), and the deoxidation products SiO2 and Al2O3 enter the slag, which reduces the R and leads to the destruction of the P reaction equilibrium. (V) Slag tapping operation shall be carried out during tapping. (V) In the later stage of blowing, the process of carbon oxidation is that the decarburization reaction decreases and the velocity decreases linearly with the blowing time. (V) At the beginning of blowing, Si and Mn are rapidly oxidized to very low levels and continue to be blown. They are no longer oxidized, while Mn is slightly recovered at the later stage of blowing. (V) Large capacity converter oxygen lance often adopts porous Laval type nozzle. (V) Nitrogen and vanadium can form vanadium nitride to refine grain. (V) When the amount of [Si] in molten iron is very high, the gun position should be higher. (x) Slag tapping is beneficial to accurately control the composition of molten steel and reduce the phosphorus content of molten steel. (V) When blowing the gas at the bottom, the blowing gas is generally blowing before the second half, and the latter half is blowing argon. (V) Hanging and blowing will accumulate (TFe) in slag, which will cause explosive splash. (V) Quantitative loading is to keep the amount of loading unchanged