高吸水性树脂可控合成工艺研究.pdfVIP

Hans Journal of Chemical Engineering and Technology 化学工程与技术, 2017, 7(1), 1-7 Published Online January 2017 in Hans. /journal/hjcet /10.12677/hjcet.2017.71001 Study on Synthesis of Super Absorbent Resin Xuan Wang, Miaofeng Liu, Shibiao Zong, Jun Ma* School of Chemistry and Chemical Engineering, Linyi University, Linyi Shandong th th th Received: Dec. 25 , 2016; accepted: Jan. 9 , 2017; published: Jan. 12 , 2017 Abstract In this paper, acrylic monomers were used as raw material; water absorbent polyacrylic acid was synthesized by inverse suspension polymerization; and the factors of resin synthesis process and process conditions were studied. The results showed that the factors such as temperature, initia- tor amount, neutralization degree of polymerization monomer, amount of crosslinking agent and other factors had significant influence on the water absorption performance. On this basis, a sili- cate of magnesium lithium superabsorbent resin was prepared, and the water absorption proper- ties were studied. The research results of this paper can provide basic data for the preparation of lithium magnesium silicate based inorganic organic composite resin. Keywords Super Absorbent Polymer, Acroleic Acid, Inverse Phase Suspension Polymerization, Hectorite 高吸水性树脂可控合成工艺研究 王 璇，刘苗凤，宗世彪，马 军* 临沂大学化学化工学院，山东 临沂 收稿日期：2016年12月25 日；录用日期：2017年1月9 日；发布日期：2017年1月12 日 摘 要 本文以丙烯酸单体为原料，采用反相悬浮聚合法合成了聚丙烯酸吸水树脂，并对树脂合成过程的工艺条 件及影响因素进行了研究。结果表明温度、引发剂用量、聚合单体中和度、交联剂用量等因素对吸水性 *通讯作者。 文章引用: 王璇, 刘苗凤, 宗世彪, 马军. 高吸水性树脂可控合成工艺研究[J]. 化学工程与技术, 2017, 7(1): 1-7. /10.12677/hjcet.2017.71001 王璇 等 能的影响显著。在此基础上初步开展了硅酸镁锂基高吸水性树脂的制备，并对其吸水性能进行了初步探 讨。本文的研究结果可为硅酸镁锂基无机–有机复合树脂的制备提供基础数据。 关键词 高吸水树脂，丙烯酸，反相悬浮聚合法，硅酸镁锂 Copyright ©