鞍 钢 技 术 2016年 第 3 期 ANGANG TECHNOLOGY 总 第 399期 ( 生户卖姨^ 复吹转炉补炉技术的改进实践 刘效森 (山东钢铁股份有限公司济南分公司，山东济南250101) 摘要：介绍了济钢炼钢厂“铁块补炉法”技术的改进情况，包括护炉前的炉渣调整、渣补护 炉的操作步骤及要点等。采用优化后的“铁块补炉法”技术后，转炉护炉时间缩短至50 m in ，节 约了 30%的补炉料，吨钢成本降低0.65元。 关键词：复吹转炉；补炉;倒渣面 中图分类号:TF 702 文献标识码： A 文章编号院1006-4613(2016)03-0047-03 Practice of Improving Fettling Technology for Combined Blown Converter Liu Xiaosen (Jinan Subsidiary Company of Shandong Iron and Steel Co ., Ltd., Jinan 250101, Shandong, China) A bstract ： Technology improvements for fettling by using iron ingots in Steelmaking Plant of Jinan Iron and Steel Subsidiary Company were introduced, which included operation procedures such as slag adjustments prior to fettling and fettling by using slag. When the optimized fettling technology is put into operation in steelmaking the converter lining protection time was shortened to 50 minutes, the fettling materials was saved by 30% and the cost for steelmaking was reduced by 0.65 yuan RMB per ton steel. Key w ords ： combined blown converter ; fettling ; slag level for tapping 目前，转炉炉衬维护存在的主要问题是倒渣 济钢炼钢厂目前有3 座 120 t 顶底复吹转 面的维护，80%以上的补炉料用在了倒渣面的维 炉，装入量为155t/炉，按 137t 铁水、16 t 废钢、 护上。济钢炼钢厂通常采用“纯渣补”和“补炉料补 2 t 铁块配比装炉。主要生产碳素结构钢、低碳钢、 炉”两种补炉技术维护转炉炉衬。但“纯渣补”技术 低合金高强度钢、高耐候性结构钢、管线钢、焊瓶 需要的时间太长，每次渣补要6耀8 h ,严重影响转 钢等，其中低碳钢的比例在60%左右，出钢温度为 炉的生产效率;而“补炉料补炉”技术不仅增加耐 1 640~1 670益。转炉终渣渣样成分及碱度见表1 材消耗，而且补第一炉时转炉炉渣化渣困难，钢水 所示。 夹杂物增加，铸机时常发生絮流或报警事故。“铁 表 1 转炉终渣成分及碱度 块补炉法”优化了转炉补炉作业方式，提高了转炉 棕[CaO ]/ 棕[SiO2]/ 棕