攀钢连铸板坯非金属夹杂物现状调查.pdfVIP

第 20 卷第 1 期 钢 　铁 　钒 　钛 Vol. 20 ,No. 1 1999 年 3 月 　　　　　　　　 IRON STEEL VANADIUM TITAN IUM 　　　　　　　　 March 1999 攀钢连铸板坯非金属夹杂物现状调查 　　严学模 　杜德信 　陈　渝 　仲剑丽 　　　　王地君 　　　　 ( ) ( ) 　　　　 攀枝花钢铁研究院 　　　　 攀钢提钒炼钢厂 摘 　要 　根据对攀钢连铸板坯中非金属夹杂物现状的调查 ,了解了 09CuPRe-B 钢连铸坯中夹杂物 的状况及在生产过程中的变化情况 ,得到的结果可作为攀钢生产洁净钢的依据 。 关键词 　连铸板坯 　球形夹杂物 　洁净钢 INVESTIGATION OF NONMETALL IC INCL USIONS IN CONTINUOUS CAST SLAB PROD UCED AT PANGANG Yan Xuemo 　Du Dexin 　Chen Yu 　Zhong Jianli ( Panzhihua Iron Steel Research Institute) Wang Dijun (VRecovery and Steelmaking Plant of Pangang) Abstract 　Based on the results of investigation on nonmetallic inclusions in continuous cast slab pro duced at pangang ,nonmetallic inclusions situation in continuous cast slab of 09CuPReB steel and their change during production were understood. The results obtained are used as the basis of clean steel pro duction at Pangang. Key Words 　continuous cast slab ,spheroidal inclusions ,clean steel 1 　引言 1 350 mm两机两流板坯连铸机 ,生产工艺流 众所周知 ,连铸坯中非金属夹杂物的种 程如图 1 所示 。 类 、数量 、尺寸及分布是衡量连铸坯质量的一 个重要指标 。近年来 ,钢铁市场竞争 日益激 烈 ,用户对钢材质量要求也越来越高 ,为改善 铸坯质量 ,扩大连铸品种和满足用户的高要 求 ,攀钢与东北大学共同研究了攀钢现工艺 条件下连铸坯非金属夹杂物的现状及其来 源 。本文主要针对攀钢 09CuPRe 连铸坯中 非金属夹杂物的现状及生产过程中夹杂物变 图 1 　攀钢炼钢 —连铸工艺流程 化情况进行分析和探讨 。 　　试验方法如下 : 2 　工艺条件和试验方法 试验在中间包的一个浇次上进行 ,共浇 攀钢转炉公称容量 120 t , 铸机型号为 5 炉 ,铸坯总长 1885 m ,钢种为 09CuPReB 。 第 1 期 　　　　　　　　严学模等 :攀钢连铸板坯非金属夹杂物现状调查