Journal of Materials Processing Technology 210 (2010) 899–906 Contents lists available at ScienceDirect Journal of Materials Processing Technology j o u rn al h omepage: w w w. elsev /locate/jmat protec Grinding characteristics in high speed grinding of engineering ceramics with brazed diamond wheels Jianyi Chen, Jianyun Shen, Hui Huang, Xipeng Xu ∗ Key Research Lab for Stone Machining, Huaqiao University, Quanzhou, Fujian 362021, China a r t i c l e i n f o a b s t r a c t Article history: An investigation was undertaken to explore the grinding characteristics and removal mechanisms in high Received 20 June 2009 speed grinding of three engineering ceramics—alumina, silicon nitride, and zirconia—by using brazed Received in revised form 2 February 2010 diamond wheels of two different grit sizes. The grinding forces and surface roughness were measured Accepted 2 February 2010 and the morphological features of ground workpiece surfaces were examined. The results indicate that material removal mechanisms are different for the three ceramics at high grinding speeds. For alumina, the removal is dominated by brittle fracture. For silicon nitride and zirconia, the ductile removal prevails Keywords: in the grinding. For each of the three ceramics, grinding power per unit width is found to be nearly High speed grinding Engineering ceramics proportional to the rate of plowed surface