再生混凝土工作性能探究.docVIP

再生混凝土工作性能探究摘 要:再生骨料混凝土技术可实现对废弃混凝土的再加工,使其恢复原有性能,形成新的建材产品,从而既能使有限资源得以利用,又解决了部分环保问题。这是发展绿色混凝土,实现建筑资源环境可持续发展的主要措施之一。本文从再生混凝土的基本概念入手,研究了再生混凝土的工作性质,以期为再生混凝土的应用研究提供借鉴 关键词:再生骨料混凝土;绿色混凝土;工作性质 中图分类号:TU528.59 文献标志码:A文章编号:1671?7953(2009)04?0062?03 Research on Regeneration Concrete Operating Performance XIAO Jun (Southwest scientific and technical university basic construction department Mianyang 621010,China) Abstract: The regeneration aggregate concrete technology may implement to abandons the concrete the retreatment, makes it to recover the original performance, forms the new building materials product, thus both can enable the restricted resource to use, and has solved the partial environmental protections problem. This is develops the green concrete, one of implementation construction resource conditions sustainable development main measures. This article obtained from the regeneration concrete basic concept, has studied the regeneration concrete work nature, as regenerated the concrete take the time the applied research to provide the model. Key words: regeneration aggregate concrete;green concrete;work nature 近二三十年来,随着我国城市化进程加快,建筑业进入高速发展阶段,大量旧建筑物达到使用年限,或由于其他因素需要拆除。一般的混凝土工程使用年限约为50-100年,我国建国初期所建成的混凝土工程己经逐步进入拆除期,21世纪将是我国混凝土结构破坏的高峰期,伴随拆除而来的是产生了大量的建筑垃圾,在建筑垃圾中作为最大宗的建筑材料一一废弃混凝土所占份额最大。因此,我们必须改变传统的混凝土生产方式,将混凝土的生产方式转变到一个可持续发展的轨道上来 1 再生混凝土的基本概念 1.1 再生混凝土的概念 再生骨料混凝土简称再生混凝土,它是指将废弃混凝土块经过破碎、清洗、分级后,按一定比例与级配混合,部分或全部代替砂石等天然骨料(主要是粗骨料)配制而成的新的混凝土。相对于再生混凝土而言,把用来生产再生骨料的原始混凝土称为基体混凝土[1] 1.2 再生混凝土的分类 再生混凝土按骨料的组合形式可以有以下几种:骨料全部为再生骨料:粗骨料为再生骨料、细骨料为天然砂;粗骨料为天然碎石或卵石、细骨料为再生骨料;再生骨料替代部分粗骨料或细骨料 2 再生混凝土的工作性质研究 2.1 用水量 再生骨料与天然骨料不同,所以再生混凝土的用水量也与天然骨料混凝土不同。再生骨料内部缺陷多,吸水率大。再者,再生骨料的表面粗糙度比天然骨料要高,因此配合比中的细骨料(砂率)较高,并随着再生骨料所取代比例的提高而增长。如图所示。由于砂率较高,因此达到相同坍落度时,比天然骨料混凝土用水要多,且难以达到坍落性能良好。图中N代表天然骨料;C代表再生骨料;G代表粗骨料:S代表细骨料;数字代表其百分含量[2] 2.2 和易性 在用水量相同的情况下,与基准混凝土相比,再生混凝土的坍落度减小,流动性变差,同时由于骨料表面粗糙,自重轻,增加了再生混凝土拌和物的摩擦阻力,使再生混凝土的粘聚性和保水性增强。研究发现,在保持用水量不变的情况下,随着再生骨料掺量的增加,混凝土的坍落度逐渐下降。只采用再生粗骨料时,