真空蒸发制备带钢锌镁合金镀层防腐蚀机制.docVIP

真空蒸发制备带钢锌镁合金镀层的防腐蚀 毛鑫光，马进沈杰 （复旦大学材料科学系上海200433） 摘 要钢板表面的锌镁合金镀层可以提高其耐腐蚀性能。本文采用真空热蒸发在镀锌钢板表面镀镁，并由快速退火工艺形成锌镁合金镀层通过电化学试验研究镀锌镁合金钢板的腐蚀过程，推断其防腐蚀机理。研究表明，在腐蚀初期，锌镁合金表面形成致密层，抗腐蚀性强的氢氧化镁致密层溶解，依靠锌层作为阳极对钢铁进行保护。 关键词 锌镁合金防腐蚀快速退火电化学真空蒸发 TG178 文献标识码 A CORROSION RESISTANT MECHANISM OF Zn-Mg ALLOY COATING ON STEEL PREPARED BY VACUUM EVAPORATION MAO Xin-guang, MA Jin, SHEN Jie* (Department of Materials Science, Fudan University, Shanghai, 200433,China) Abstract: Zn-Mg alloy coating can enhance the corrosion resistance property of steel. This study employed vacuum evaporation and short-term thermal treatment in the preparation of Mg layer on galvanized steel. The corrosion process through electrochemical analysis was studied, and the corrosion resistant mechanism was discussed. Studies show that, a dense layer forms at the top of zinc layer at the first stage of corrosion. The dense layer consists of magnesium hydroxide，zinc hydroxide and magnesium oxide, which are compact, insoluble and consequently well corrosion-resistant, and after the dense layer decomposes, zinc layer protects steel as anode. Key words: Zn-Mg Alloy; Corrosion Resistance; Fast Annealing; Electrochemistry; Vacuum Evaporation 0 引 言 收稿日期：2012-8-29 修订日期：2012-9-6 基金项目：国家自然科学基金(项目批准 作者简介：毛鑫光（1989-），男，硕士生 通讯作者：沈杰，副教授，shenjie@fudan.edu.cn，（021作为钢铁防腐蚀涂层锌基合金与纯锌相比具有更高的耐蚀性，并有良好的防护性能价格比[,]。锌镁合金由于其优异的耐腐蚀性能，日本的川崎钢铁公司[]、新日铁钢铁公司[]、神户制钢所[]和德国蒂森克虏伯钢铁公司[,]都对钢板锌镁合金镀层的制造工艺及其耐蚀性能做过报道，结果均显示锌镁合金镀层具有优异的耐腐蚀性能。就目前文献报道来看，锌镁合金镀层是目前为止耐蚀性最高的锌基合金镀层，日本神户制钢所采用真空镀法生产的锌镁合金电镀钢板与普通的镀锌钢板相比，耐蚀性提高了23倍[6]。目前，文献报道的锌镁合金镀层的制备方法主要有真空镀[,,]，水溶液电镀[]，熔融盐电镀[4,]和热浸镀[5]。其中，真空镀可沉积铝、镁等湿法电镀无法沉积的标准电极电位很负的金属，且真空镀层的附着力、致密度、硬度、耐腐蚀性等都相当优良。因此真空蒸发制备锌镁合金镀层将是今后钢铁防腐蚀镀层制备工艺中值得重视的一项新技术[]。 国内外钢板上锌镁合金镀层的研究还属刚刚起步阶段，其制造工艺和耐蚀机理的研究尚不成熟和完善有研究表明，锌镁金属间化合物MgZn2和Mg2Zn11的形成可能是其耐腐蚀性能提高的主要原因[58,9]，而对真空蒸发后快速退火制备锌镁合金的合金化过程及其防腐蚀机理的研究还很少。目前，对锌镁合金[,,]的防腐蚀机制的研究主要集中在非真空镀的方法，真空镀法锌镁合金镀层 []采用盐雾试验法，Klemm[]采用电化学方法，但制备方法是利