PMI高性能泡沫夹层材料的应用及国内研制现状(外国英语资料).docVIP

PMI高性能泡沫夹层材料的应用及国内研制现状 360. Composites Innovation and sustainable development Application and development status of PMI high performance foam sandwich materials Yi Ming Chen 1 bin he 2 ( 1. 、 School of aerospace and materials engineering, National University of Defense Technology, Changsha 410073; 2. 、 Hunan Plastics Research Institute, Changsha 410001) Poly (methyl imide) imide is described in this paper ( PMI) application and development of foam sandwich materials in china. Key word PMI foam Sandwich structure Preparation Application Introduction Composite material and its structure is one of the key timber and load-bearing structures of aircraft. In order to improve the mechanical properties of composite materials, it is fully beneficial With the strength of the material and the weight of the structure, a lot of foam sandwich composite materials are used in the structural parts of the aircraft. Poly propylene Imide ( (PMI) foam, with its outstanding overall performance, in large passenger aircraft and transport planes, fighter aircraft, helicopters, high-speed trains, wind turbines Blades, satellites, and launch vehicles, as well as sports and medical equipment, have been widely used. Two PMI foam properties Poly imide imide ( PMI) foam is all high polymer foam The highest specific strength of the foam, and its superior overall performance is shown in : Foam The surface is smooth, the structure and mechanical properties are non directional, and can be machined and resistant Organic solvent and compatible with various resin systems High specific strength, high fever deformation temperature ( 180 DEG C ~ 200 c ) and excellent compressive creep resistance, Specific compressive strength of PMI foam (Fig. One ) make it affordable 180 DEG C ~ Dimensional stability of foam cured by resin curing process at 200 Requirement。 At the same time, PMI foams have thermal deformation properties, depending on the composite material The requirements of foam sandwich shape were prep