退火对(nd,pr)128dy02fe774co40b56 快淬薄带晶化行为的影响.pdfVIP

44 10 Vol.44, No.10 2015 10 RARE METAL MATERIALS AND ENGINEERING October 2015 (Nd,Pr)12.8Dy0.2Fe77.4Co4.0B5.6 ( , 315211) DSC (Nd,Pr)12.8Dy0.2Fe77.4 Co4.0B5.6 (Nd,Pr)12.8Dy0.2Fe77.4 Co4.0B5.6 30 K/min DSC 865.8 K 877.2 K 901.7 K 581.2 K 1003.6 K 10 min 803.0 K DSC 693.0~743.0 K 803.0 K 10~40 K/min 1.4%20~40 K/min Nd-Fe-B TG132.2+7 A 1002-185X(2015)10-2544-05 95%(, )NdDy Pr 99.5%Co FeFe-20%B [1] Ar 3 [2] (Nd,Pr)12.8Dy0.2Fe77.4Co4.0B5.6 LZK-12A [3] 35 m/s NETZSCH DSC 404F1 DSC 10, 20, 30, 40 K/min DSC 50 mL/min 10, 20, 30, 40 K/min DSC (Nd,Pr)12.8Dy0.2Fe77.4Co4.0B5.6 PtRh 30 K/min DSC 30 PrDy Nd Pr Nd [4] K/min 5, 10 Pr Fe BDy Fe B Nd Fe B min 2 14 2 14 2 14 [5] [6,7] Co Fe DSC D8Focus X (Cu Kα) X