一起干式铁心串联电抗器烧损原因浅析及处理 电工电气 (20 17 No.5) 一起干式铁心串联电抗器烧损原因浅析及处理 朱丽华 (常州东芝舒电变压器有限公司，江苏 常州 213012) 摘 要：针对一起干式铁心串联电抗器烧损的事故，通过对烧损的串联电抗器进行解体检查，结合 产品运行期间出现的温升及噪声过高的问题展开分析，认为引起电抗器烧损及噪声大的主要原因是由于 铁心材质存在问题，并提出了检修实施方案，产品重新投入运行后，引起铁心串联电抗器温度过高及噪 声大的主要原因已基本排除。 关键词：电抗器；铁心；温升；噪声 中图分类号：TM471 文献标识码：B 文章编号：1007-3175(2017)05-0041-03 Elementary Analysis and Treatment of a Case of Dry-Type Iron Core Series Reactor Burned Loss Cause ZHU Li-hua Changzhou Toshiba Shudian Transformer Co., Ltd, Changzhou 2 13012, China （ ） Abstract: This paper took the examination on the disintegrated parts of burned loss series reactors and carried out analysis for problems of fast temperature rise and loud noises during operation. The main reason causing series reactors burned loss and loud noises were the problem of iron core material. The overhaul embodiment was proposed and its effect was verified. Key words: reactor; core; temperature rise; noise 0 引言 某变压器检修公司承接了一台烧损的CKSG- 1200/10三相干式串联电抗器修复任务。这是一台 带气隙铁心串联电抗器具有稳定、足够大的电 F级无抽头电感固定式带气隙干式铁心电抗器，绝 感量，可抑制大电流冲击性负载运行对电网的影 缘耐热温度为155℃，线圈为单层圆筒式结构，采 响，在钢铁、铸造等行业得到了广泛应用。由于串 用环氧玻璃丝线包绝缘扁导线加工而成，线圈与铁 联电抗器结构特点及负载特性，使得产品在运行过 心间用薄型环氧玻璃布板作绝缘。 程中经常承受由过电压和冲击电流等对电气绝缘的 从用户处了解得知：该电抗器是一台已经检 侵害，运行噪声大，相比较常规电力变压器更容易 修过的进口设备。自检修后重新投入使用，运行 损坏。 人员即发现该电抗器运行时存在两大问题：一是 本文通过对一起干式串联电抗器烧损故障原因 噪声大；二是温度高，最高时超过了200℃。在 展开分析，认为引起电抗器烧损及噪声过大的主要 用户多次要求下，原负责检修的变压器生产厂家 原因是由于铁心材质存在问题，提高质量意识，严