书下1111.PDF

熱可塑性ナノコンポジット光学材料の開発 大林　達彦 ＊，鈴木　亮＊＊，望月　宏顕＊，相木　康弘＊ Development of Thermoplastic Nanocomposite Optical Materials Tatsuhiko OBAYASHI*, Ryo SUZUKI**, Hiroaki MOCHIZUKI*, and Yasuhiro AIKI* Abstract Thermoplastic nanocomposite optical materials that include ZrO nanoparticles in high concentration 2 have been developed. Even after undergoing the melt-molding processing, homogeneous dispersion of nanoparticles in the resin was maintained and the molded articles showed good transparency. The refractive index of the resin rose from 1.59 to 1.65 by the addition of 12.5 vol% ZrO nanoparticles. It was found that 2 the kinds and number of functional groups in polymer, the length of linkers between the functional groups and the main chain of the polymer were very important to achieve the homogeneous dispersion of particles and the moldability of the nanocomposite. This material was molded into convex and concave lenses. 111 はじめに 硫黄，重金属原子，芳香環などを導入することにより分 極率を高める分子設計が一般的であるが 1），2） ，該高屈 「屈折率」はレンズなどの光学部品において，最も重 折率化手段は吸収波長の長波化につながるため，透明材 要な基本特性の一つである。屈折率の制御は，光の速度・ 料を設計する上では限界がある。また，「酸化による耐 進路を操作し，「光を加工する」ための重要な技術であり， 熱着色性の悪化」，「吸水性上昇」など別の問題とも相関 高・低屈折率材料の追及，アッベ数（屈折率の波長依存 するため注意が必要である。 性）制御，複屈折（屈折率の異方性）制御などの材料研 樹脂単独での屈折率向上には限界があるため，別の手 究が活発に続けられている。 段として屈折率の高い無機材料を樹脂に複合する手段も 高屈折率材料をレンズに用いた場合には，小さな曲率で 検討されてきた 3）～ 6）