石膏掺量对硅酸盐和硫铝酸盐水泥复合体系性能的影响.pdfVIP

实验与研究 石膏掺量对硅酸盐和硫铝酸盐水泥复合体系性能的影响 The influence of amount of gypsum on performance of Portland-sulphoalminate composite cement system 李炳良 （陕西铁路工程职业技术学院，陕西渭南714000 ） 摘要：硅酸盐水泥与硫铝酸盐水泥复合后水泥的矿物组成变得多而复杂，这种复合体系水泥的水化硬化过程 是一个多元复杂体系的多种矿物的水化硬化过程。 将硫铝酸盐水泥熟料、硅酸盐水泥、无水石膏以合适的比例 混合，通过试验和分析，制得早期强度相近、28d 强度接近或超过纯硫铝酸盐水泥的复合胶凝体系，得出石膏的 最佳掺量。 关键词：凝结时间；抗压强度；抗折强度；体积稳定性 Abstract:Sulphoaluminate cement and Portland cement composite of the mineral composition of cement has become more complex,this complex system of cement hydration and hardening process is a diverse and complex system of multi-mineral hydration and hardening process.the sulphoaluminate cement clinker,Portland cement and anhydrous gypsum in a suitable ratio of mixing,through testing and analyzing,composite gel system that the early strength and 28 days strength be close to or more than sulphoaluminate cement can be prepared,and we arrive at the optimal dosage of gypsum. Key words:setting time;compressive strength;bending strength;volume stability 中图分类号： 文献标识码： 文章编号： （ ） TQ172.71+8 B 1003-8965 2009 06-0069-05 1 引言 系统。 将硫铝酸盐水泥熟料、硅酸盐水泥、无水石膏 以合适的比例混合， 以期制得早期强度相近、28d 硅酸盐水泥与硫铝酸盐水泥复合后水泥的矿 强度接近或超过纯硫铝酸盐水泥的复合胶凝体系。 物组成变得多而复杂，且水化产物中除硅酸盐水泥 该复合胶凝体系的主要水化产物是钙矾石、 铝胶、 水化产物外，还有硫铝酸盐水泥的水化产物，并且 CSH 凝胶和少量低硫型水化硫铝酸钙， 钙矾石的 二者的水化还会相互影响。 本文研究的由硅酸盐水 形成提供了复合胶凝体系的早期强度， 而CSH 的 [1] 泥 硫铝酸盐水泥熟料 无水石膏所组成的三元复 形成，保证了水泥后期强度的增长 。 因此，其长期 － － 合体系，其