开姆洛克粘结原理（Open mlock bonding principle）.docVIP

开姆洛克粘结原理（Open mlock bonding principle） Principle of bonding: (1) on the low modulus between rubber and metal of high modulus of adhesive should become a modulus gradient layer, to reduce the bonding force when the stress concentration, so the thickness of adhesive layer should have certain. The base coating adhesive modulus is always greater than the surface coating adhesive modulus, and the surface coating adhesive modulus is generally greater than that of rubber. (2) between the base coat adhesive and the single coated adhesive, adhesive and rubber are bonded by mutual diffusion and co-crosslinking. The diffusion of adhesives and rubber interfaces is very important for fine bonding. Sufficient mutual diffusion can form a completely continuous transition layer between adhesives and rubber. The mutual diffusion ability should be considered when designing adhesive. There is sufficient mutual diffusion time before the crosslinking reaction occurs. (3) when the adhesive is designed, the following sequence should occur. A, base coat, surface coated adhesive internal crosslinking and co-crosslinking. B, base coated adhesive and metal adsorption C, adhesives and rubber produce copiers, rubber crosslinks. The adhesion of rubber and fiber and fabric is similar. Selection principle First of all, it is advisable to choose a double coating system for the factory with double coated or single coating, demanding high product or metal surface treatment process. The metal area is as follows: varieties Square meters/Kg varieties Square meters/Kg varieties Square meters/Kg CH205 15-20 CH218 5-10 CH238 5-10 CH220 14 -- 18 CH236 5-10 CH250 7-14 CH252 5-8 CH607 30 CH608 30 (metal surface treatment with 40 eyes) At least 10 factors should be considered when choosing a specific breed after determining a single or double-coated system: 1. The degree of adhesion and adhesion is also different. The adhesion performance of general rubber is different, and the viscosity index can be used to in